EN 1.7231 Steel vs. CC762S Brass

EN 1.7231 steel belongs to the iron alloys classification, while CC762S brass belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.7231 steel and the bottom bar is CC762S brass.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 240 to 280
210
Elastic (Young's, Tensile) Modulus, GPa 190
110
Elongation at Break, % 11 to 12
7.3
Poisson's Ratio 0.29
0.32
Shear Modulus, GPa 73
43
Tensile Strength: Ultimate (UTS), MPa 790 to 930
840
Tensile Strength: Yield (Proof), MPa 570 to 800
540

Thermal Properties

Latent Heat of Fusion, J/g 250
200
Maximum Temperature: Mechanical, °C 420
160
Melting Completion (Liquidus), °C 1460
920
Melting Onset (Solidus), °C 1420
870
Specific Heat Capacity, J/kg-K 470
420
Thermal Conductivity, W/m-K 46
51
Thermal Expansion, µm/m-K 13
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
28
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
32

Otherwise Unclassified Properties

Base Metal Price, % relative 2.5
24
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 1.5
3.1
Embodied Energy, MJ/kg 20
51
Embodied Water, L/kg 51
350

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 87 to 100
54
Resilience: Unit (Modulus of Resilience), kJ/m3 870 to 1700
1290
Stiffness to Weight: Axial, points 13
7.8
Stiffness to Weight: Bending, points 24
20
Strength to Weight: Axial, points 28 to 33
29
Strength to Weight: Bending, points 24 to 27
25
Thermal Diffusivity, mm2/s 12
15
Thermal Shock Resistance, points 23 to 27
27

Alloy Composition

Aluminum (Al), % 0
3.0 to 7.0
Antimony (Sb), % 0
0 to 0.030
Carbon (C), % 0.38 to 0.45
0
Chromium (Cr), % 0.8 to 1.2
0
Copper (Cu), % 0
57 to 67
Iron (Fe), % 96.4 to 98.1
1.5 to 4.0
Lead (Pb), % 0
0 to 0.2
Manganese (Mn), % 0.6 to 1.0
2.5 to 5.0
Molybdenum (Mo), % 0.15 to 0.3
0
Nickel (Ni), % 0
0 to 3.0
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 0 to 0.6
0 to 0.1
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
0 to 0.2
Zinc (Zn), % 0
13.4 to 36