EN 1.7233 Steel vs. EN 1.4029 Stainless Steel
Both EN 1.7233 steel and EN 1.4029 stainless steel are iron alloys. They have 88% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is EN 1.7233 steel and the bottom bar is EN 1.4029 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 18 to 23 | |
| 10 to 20 |
| Fatigue Strength, MPa | 270 to 530 | |
| 270 to 400 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 76 |
| Shear Strength, MPa | 450 to 590 | |
| 440 to 550 |
| Tensile Strength: Ultimate (UTS), MPa | 700 to 960 | |
| 700 to 930 |
| Tensile Strength: Yield (Proof), MPa | 380 to 780 | |
| 410 to 740 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 430 | |
| 750 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1440 |
| Melting Onset (Solidus), °C | 1420 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 39 | |
| 30 |
| Thermal Expansion, µm/m-K | 13 | |
| 10 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.4 | |
| 3.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.5 | |
| 3.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 3.0 | |
| 7.0 |
| Density, g/cm3 | 7.8 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 1.6 | |
| 2.0 |
| Embodied Energy, MJ/kg | 21 | |
| 28 |
| Embodied Water, L/kg | 53 | |
| 100 |
Common Calculations
| PREN (Pitting Resistance) | 3.3 | |
| 14 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 200 | |
| 89 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 380 to 1630 | |
| 440 to 1410 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 25 to 34 | |
| 25 to 33 |
| Strength to Weight: Bending, points | 22 to 28 | |
| 23 to 27 |
| Thermal Diffusivity, mm2/s | 11 | |
| 8.1 |
| Thermal Shock Resistance, points | 21 to 28 | |
| 26 to 34 |
Alloy Composition
| Carbon (C), % | 0.39 to 0.45 | |
| 0.25 to 0.32 |
| Chromium (Cr), % | 1.2 to 1.5 | |
| 12 to 13.5 |
| Iron (Fe), % | 96.2 to 97.5 | |
| 82.8 to 87.6 |
| Manganese (Mn), % | 0.4 to 0.7 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0.5 to 0.7 | |
| 0 to 0.6 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.035 | |
| 0.15 to 0.25 |