EN 1.7240 Steel vs. SAE-AISI D3 Steel

Both EN 1.7240 steel and SAE-AISI D3 steel are iron alloys. They have 86% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.7240 steel and the bottom bar is SAE-AISI D3 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
74
Tensile Strength: Ultimate (UTS), MPa 670 to 1990
770 to 2050

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Melting Completion (Liquidus), °C 1460
1430
Melting Onset (Solidus), °C 1410
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 44
31
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
3.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
3.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
8.0
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.5
3.2
Embodied Energy, MJ/kg 20
48
Embodied Water, L/kg 50
100

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 24 to 71
28 to 74
Strength to Weight: Bending, points 22 to 45
24 to 47
Thermal Diffusivity, mm2/s 12
8.3
Thermal Shock Resistance, points 20 to 59
23 to 63

Alloy Composition

Carbon (C), % 0.56 to 0.64
2.0 to 2.4
Chromium (Cr), % 0.7 to 1.0
11 to 13.5
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 96.7 to 97.9
80.3 to 87
Manganese (Mn), % 0.7 to 1.0
0 to 0.6
Molybdenum (Mo), % 0.15 to 0.25
0
Nickel (Ni), % 0
0 to 0.3
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 0 to 0.4
0 to 0.6
Sulfur (S), % 0 to 0.025
0 to 0.030
Tungsten (W), % 0
0 to 1.0
Vanadium (V), % 0
0 to 1.0

Comparable Variants