EN 1.7335 Steel vs. EN 1.4378 Stainless Steel
Both EN 1.7335 steel and EN 1.4378 stainless steel are iron alloys. They have 67% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is EN 1.7335 steel and the bottom bar is EN 1.4378 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 150 to 160 | |
| 190 to 340 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 21 to 22 | |
| 14 to 34 |
| Fatigue Strength, MPa | 200 to 220 | |
| 340 to 550 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 77 |
| Shear Strength, MPa | 310 to 330 | |
| 510 to 680 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 520 | |
| 760 to 1130 |
| Tensile Strength: Yield (Proof), MPa | 280 to 310 | |
| 430 to 970 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 290 |
| Maximum Temperature: Mechanical, °C | 430 | |
| 910 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1390 |
| Melting Onset (Solidus), °C | 1420 | |
| 1350 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Expansion, µm/m-K | 13 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.8 | |
| 12 |
| Density, g/cm3 | 7.9 | |
| 7.6 |
| Embodied Carbon, kg CO2/kg material | 1.6 | |
| 2.7 |
| Embodied Energy, MJ/kg | 21 | |
| 39 |
| Embodied Water, L/kg | 52 | |
| 150 |
Common Calculations
| PREN (Pitting Resistance) | 2.7 | |
| 23 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 91 to 97 | |
| 150 to 220 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 210 to 260 | |
| 470 to 2370 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 18 | |
| 28 to 41 |
| Strength to Weight: Bending, points | 18 | |
| 24 to 31 |
| Thermal Shock Resistance, points | 15 | |
| 16 to 23 |
Alloy Composition
| Carbon (C), % | 0.080 to 0.18 | |
| 0 to 0.080 |
| Chromium (Cr), % | 0.7 to 1.2 | |
| 17 to 19 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 |
| Iron (Fe), % | 96.4 to 98.4 | |
| 61.2 to 69 |
| Manganese (Mn), % | 0.4 to 1.0 | |
| 11.5 to 14.5 |
| Molybdenum (Mo), % | 0.4 to 0.6 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 2.3 to 3.7 |
| Nitrogen (N), % | 0 to 0.012 | |
| 0.2 to 0.4 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.060 |
| Silicon (Si), % | 0 to 0.35 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.030 |