EN 1.7361 Steel vs. N06210 Nickel

EN 1.7361 steel belongs to the iron alloys classification, while N06210 nickel belongs to the nickel alloys. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.7361 steel and the bottom bar is N06210 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
220
Elongation at Break, % 11
51
Fatigue Strength, MPa 480
320
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
85
Shear Strength, MPa 600
560
Tensile Strength: Ultimate (UTS), MPa 1010
780
Tensile Strength: Yield (Proof), MPa 780
350

Thermal Properties

Latent Heat of Fusion, J/g 250
330
Maximum Temperature: Mechanical, °C 470
980
Melting Completion (Liquidus), °C 1460
1570
Melting Onset (Solidus), °C 1420
1510
Specific Heat Capacity, J/kg-K 470
420
Thermal Expansion, µm/m-K 13
12

Otherwise Unclassified Properties

Base Metal Price, % relative 3.6
85
Density, g/cm3 7.8
9.0
Embodied Carbon, kg CO2/kg material 1.7
17
Embodied Energy, MJ/kg 22
250
Embodied Water, L/kg 60
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
320
Resilience: Unit (Modulus of Resilience), kJ/m3 1590
280
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
22
Strength to Weight: Axial, points 36
24
Strength to Weight: Bending, points 29
21
Thermal Shock Resistance, points 29
22

Alloy Composition

Carbon (C), % 0.28 to 0.35
0 to 0.015
Chromium (Cr), % 2.8 to 3.3
18 to 20
Cobalt (Co), % 0
0 to 1.0
Iron (Fe), % 94.1 to 96.2
0 to 1.0
Manganese (Mn), % 0.4 to 0.7
0 to 0.5
Molybdenum (Mo), % 0.3 to 0.5
18 to 20
Nickel (Ni), % 0 to 0.6
54.8 to 62.5
Phosphorus (P), % 0 to 0.035
0 to 0.020
Silicon (Si), % 0 to 0.4
0 to 0.080
Sulfur (S), % 0 to 0.035
0 to 0.020
Tantalum (Ta), % 0
1.5 to 2.2
Vanadium (V), % 0
0 to 0.35