EN 1.7365 Steel vs. AISI 414 Stainless Steel

Both EN 1.7365 steel and AISI 414 stainless steel are iron alloys. They have a moderately high 91% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.7365 steel and the bottom bar is AISI 414 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 18
17
Fatigue Strength, MPa 320
430 to 480
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
76
Tensile Strength: Ultimate (UTS), MPa 700
900 to 960
Tensile Strength: Yield (Proof), MPa 470
700 to 790

Thermal Properties

Latent Heat of Fusion, J/g 260
280
Maximum Temperature: Mechanical, °C 510
750
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 40
25
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.2
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 9.4
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 4.4
8.0
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.8
2.1
Embodied Energy, MJ/kg 24
29
Embodied Water, L/kg 70
100

Common Calculations

PREN (Pitting Resistance) 6.8
13
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
140 to 150
Resilience: Unit (Modulus of Resilience), kJ/m3 580
1260 to 1590
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 25
32 to 34
Strength to Weight: Bending, points 22
27 to 28
Thermal Diffusivity, mm2/s 11
6.7
Thermal Shock Resistance, points 20
33 to 35

Alloy Composition

Carbon (C), % 0.12 to 0.19
0 to 0.15
Chromium (Cr), % 4.0 to 6.0
11.5 to 13.5
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 91.2 to 94.9
81.8 to 87.3
Manganese (Mn), % 0.5 to 0.8
0 to 1.0
Molybdenum (Mo), % 0.45 to 0.65
0
Nickel (Ni), % 0
1.3 to 2.5
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.8
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.030
Vanadium (V), % 0 to 0.050
0