EN 1.7366 Steel vs. AWS BVAu-7

EN 1.7366 steel belongs to the iron alloys classification, while AWS BVAu-7 belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown.

For each property being compared, the top bar is EN 1.7366 steel and the bottom bar is AWS BVAu-7.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
130
Poisson's Ratio 0.29
0.38
Shear Modulus, GPa 74
45
Tensile Strength: Ultimate (UTS), MPa 460 to 710
200

Thermal Properties

Latent Heat of Fusion, J/g 260
140
Melting Completion (Liquidus), °C 1460
1120
Melting Onset (Solidus), °C 1420
1100
Specific Heat Capacity, J/kg-K 470
240
Thermal Expansion, µm/m-K 13
13

Otherwise Unclassified Properties

Density, g/cm3 7.8
15

Common Calculations

Stiffness to Weight: Axial, points 14
4.7
Stiffness to Weight: Bending, points 25
11
Strength to Weight: Axial, points 16 to 25
3.7
Strength to Weight: Bending, points 17 to 23
5.1
Thermal Shock Resistance, points 13 to 20
8.9

Alloy Composition

Cadmium (Cd), % 0
0 to 0.0010
Carbon (C), % 0 to 0.18
0 to 0.0050
Chromium (Cr), % 4.0 to 6.0
0
Cobalt (Co), % 0
0 to 0.060
Gold (Au), % 0
49.5 to 50.5
Iron (Fe), % 91.9 to 95.3
0
Lead (Pb), % 0
0 to 0.0020
Manganese (Mn), % 0.3 to 0.8
0
Molybdenum (Mo), % 0.45 to 0.65
0
Nickel (Ni), % 0
24.5 to 25.5
Palladium (Pd), % 0
23.9 to 26
Phosphorus (P), % 0 to 0.025
0 to 0.0020
Silicon (Si), % 0 to 0.4
0
Sulfur (S), % 0 to 0.015
0
Zinc (Zn), % 0
0 to 0.0010