EN 1.7366 Steel vs. EN 1.0225 Steel

Both EN 1.7366 steel and EN 1.0225 steel are iron alloys. They have a moderately high 94% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.7366 steel and the bottom bar is EN 1.0225 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140 to 210
130 to 140
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 17 to 19
6.7 to 24
Fatigue Strength, MPa 160 to 320
170 to 220
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Shear Strength, MPa 290 to 440
280 to 290
Tensile Strength: Ultimate (UTS), MPa 460 to 710
440 to 500
Tensile Strength: Yield (Proof), MPa 230 to 480
230 to 380

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 510
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
52
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.1
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 9.3
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 4.3
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.7
1.4
Embodied Energy, MJ/kg 23
18
Embodied Water, L/kg 69
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 74 to 110
31 to 95
Resilience: Unit (Modulus of Resilience), kJ/m3 140 to 600
140 to 390
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 16 to 25
16 to 18
Strength to Weight: Bending, points 17 to 23
16 to 18
Thermal Diffusivity, mm2/s 11
14
Thermal Shock Resistance, points 13 to 20
14 to 16

Alloy Composition

Carbon (C), % 0 to 0.18
0 to 0.21
Chromium (Cr), % 4.0 to 6.0
0
Iron (Fe), % 91.9 to 95.3
98 to 100
Manganese (Mn), % 0.3 to 0.8
0 to 1.4
Molybdenum (Mo), % 0.45 to 0.65
0
Phosphorus (P), % 0 to 0.025
0 to 0.045
Silicon (Si), % 0 to 0.4
0 to 0.35
Sulfur (S), % 0 to 0.015
0 to 0.045

Comparable Variants