EN 1.7366 Steel vs. Solder Alloy 114
EN 1.7366 steel belongs to the iron alloys classification, while solder alloy 114 belongs to the otherwise unclassified metals. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is EN 1.7366 steel and the bottom bar is solder alloy 114.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 140 to 210 | |
| 12 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 30 |
| Elongation at Break, % | 17 to 19 | |
| 25 |
| Poisson's Ratio | 0.29 | |
| 0.41 |
| Shear Modulus, GPa | 74 | |
| 11 |
| Tensile Strength: Ultimate (UTS), MPa | 460 to 710 | |
| 37 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 38 |
| Melting Completion (Liquidus), °C | 1460 | |
| 240 |
| Melting Onset (Solidus), °C | 1420 | |
| 180 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 170 |
| Thermal Conductivity, W/m-K | 40 | |
| 44 |
| Thermal Expansion, µm/m-K | 13 | |
| 26 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 8.1 | |
| 10 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.3 | |
| 9.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 4.3 | |
| 95 |
| Density, g/cm3 | 7.8 | |
| 9.7 |
| Embodied Carbon, kg CO2/kg material | 1.7 | |
| 8.3 |
| Embodied Energy, MJ/kg | 23 | |
| 140 |
| Embodied Water, L/kg | 69 | |
| 760 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 1.7 |
| Stiffness to Weight: Bending, points | 25 | |
| 11 |
| Strength to Weight: Axial, points | 16 to 25 | |
| 1.1 |
| Strength to Weight: Bending, points | 17 to 23 | |
| 2.6 |
| Thermal Diffusivity, mm2/s | 11 | |
| 27 |
| Thermal Shock Resistance, points | 13 to 20 | |
| 3.4 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0010 |
| Antimony (Sb), % | 0 | |
| 0 to 0.5 |
| Arsenic (As), % | 0 | |
| 0 to 0.030 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.25 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0050 |
| Carbon (C), % | 0 to 0.18 | |
| 0 |
| Chromium (Cr), % | 4.0 to 6.0 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.080 |
| Gold (Au), % | 0 | |
| 0 to 0.050 |
| Indium (In), % | 0 | |
| 0 to 0.1 |
| Iron (Fe), % | 91.9 to 95.3 | |
| 0 to 0.020 |
| Lead (Pb), % | 0 | |
| 58.4 to 60.5 |
| Manganese (Mn), % | 0.3 to 0.8 | |
| 0 |
| Molybdenum (Mo), % | 0.45 to 0.65 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 0 to 0.010 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 |
| Silver (Ag), % | 0 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Tin (Sn), % | 0 | |
| 39.5 to 40.5 |
| Zinc (Zn), % | 0 | |
| 0 to 0.0010 |