EN 1.7367 Steel vs. EN 1.1118 Cast Steel

Both EN 1.7367 steel and EN 1.1118 cast steel are iron alloys. They have 90% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.7367 steel and the bottom bar is EN 1.1118 cast steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 18
14 to 21
Fatigue Strength, MPa 310
320 to 400
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 75
73
Tensile Strength: Ultimate (UTS), MPa 670
700 to 750
Tensile Strength: Yield (Proof), MPa 460
460 to 630

Thermal Properties

Latent Heat of Fusion, J/g 270
250
Maximum Temperature: Mechanical, °C 600
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 26
51
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.9
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 10
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 7.0
1.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.6
1.4
Embodied Energy, MJ/kg 37
19
Embodied Water, L/kg 88
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
97 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 560
550 to 1050
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 24
25 to 27
Strength to Weight: Bending, points 22
22 to 23
Thermal Diffusivity, mm2/s 6.9
14
Thermal Shock Resistance, points 19
22 to 24

Alloy Composition

Aluminum (Al), % 0 to 0.020
0
Carbon (C), % 0.080 to 0.12
0.2 to 0.25
Chromium (Cr), % 8.0 to 9.5
0
Iron (Fe), % 87.3 to 90.3
97.3 to 98.3
Manganese (Mn), % 0.3 to 0.6
1.5 to 1.8
Molybdenum (Mo), % 0.85 to 1.1
0
Nickel (Ni), % 0 to 0.4
0
Niobium (Nb), % 0.060 to 0.1
0
Nitrogen (N), % 0.030 to 0.070
0
Phosphorus (P), % 0 to 0.030
0 to 0.020
Silicon (Si), % 0.2 to 0.5
0 to 0.6
Sulfur (S), % 0 to 0.010
0 to 0.015
Titanium (Ti), % 0 to 0.010
0
Vanadium (V), % 0.18 to 0.25
0
Zirconium (Zr), % 0 to 0.010
0