EN 1.7378 Steel vs. SAE-AISI H41 Steel

Both EN 1.7378 steel and SAE-AISI H41 steel are iron alloys. They have 88% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is EN 1.7378 steel and the bottom bar is SAE-AISI H41 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
77
Tensile Strength: Ultimate (UTS), MPa 700
710 to 2210

Thermal Properties

Latent Heat of Fusion, J/g 260
270
Melting Completion (Liquidus), °C 1470
1560
Melting Onset (Solidus), °C 1430
1510
Specific Heat Capacity, J/kg-K 470
450
Thermal Conductivity, W/m-K 39
28
Thermal Expansion, µm/m-K 13
12

Otherwise Unclassified Properties

Base Metal Price, % relative 4.0
18
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 2.3
6.8
Embodied Energy, MJ/kg 33
97
Embodied Water, L/kg 61
97

Common Calculations

PREN (Pitting Resistance) 5.8
35
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25
24 to 76
Strength to Weight: Bending, points 22
22 to 47
Thermal Diffusivity, mm2/s 10
7.7
Thermal Shock Resistance, points 20
20 to 64

Alloy Composition

Aluminum (Al), % 0 to 0.020
0
Boron (B), % 0.0015 to 0.0070
0
Carbon (C), % 0.050 to 0.1
0.6 to 0.75
Chromium (Cr), % 2.2 to 2.6
3.5 to 4.0
Iron (Fe), % 94.6 to 96.1
81.8 to 85
Manganese (Mn), % 0.3 to 0.7
0.15 to 0.4
Molybdenum (Mo), % 0.9 to 1.1
8.2 to 9.2
Nitrogen (N), % 0 to 0.010
0
Phosphorus (P), % 0 to 0.020
0 to 0.030
Silicon (Si), % 0.15 to 0.45
0.2 to 0.45
Sulfur (S), % 0 to 0.010
0 to 0.030
Titanium (Ti), % 0.050 to 0.1
0
Tungsten (W), % 0
1.4 to 2.1
Vanadium (V), % 0.2 to 0.3
1.0 to 1.3