EN 1.7379 Steel vs. EN 1.8527 Steel
Both EN 1.7379 steel and EN 1.8527 steel are iron alloys. Both are furnished in the quenched and tempered condition. They have a very high 98% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is EN 1.7379 steel and the bottom bar is EN 1.8527 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 200 | |
| 270 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 21 | |
| 16 |
| Fatigue Strength, MPa | 320 | |
| 520 |
| Impact Strength: V-Notched Charpy, J | 45 | |
| 39 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 74 | |
| 74 |
| Tensile Strength: Ultimate (UTS), MPa | 670 | |
| 900 |
| Tensile Strength: Yield (Proof), MPa | 460 | |
| 800 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 460 | |
| 490 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 39 | |
| 41 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.6 | |
| 7.8 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.8 | |
| 9.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 3.8 | |
| 4.0 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.8 | |
| 1.7 |
| Embodied Energy, MJ/kg | 23 | |
| 23 |
| Embodied Water, L/kg | 59 | |
| 66 |
Common Calculations
| PREN (Pitting Resistance) | 5.7 | |
| 5.7 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 120 | |
| 140 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 550 | |
| 1670 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 24 | |
| 32 |
| Strength to Weight: Bending, points | 22 | |
| 26 |
| Thermal Diffusivity, mm2/s | 11 | |
| 11 |
| Thermal Shock Resistance, points | 19 | |
| 26 |
Alloy Composition
| Carbon (C), % | 0.13 to 0.2 | |
| 0.040 to 0.12 |
| Chromium (Cr), % | 2.0 to 2.5 | |
| 3.7 to 4.3 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Iron (Fe), % | 94.5 to 96.5 | |
| 93.2 to 95.1 |
| Manganese (Mn), % | 0.5 to 0.9 | |
| 0.85 to 1.2 |
| Molybdenum (Mo), % | 0.9 to 1.2 | |
| 0.4 to 0.6 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.6 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.035 |