EN 1.7379 Steel vs. C15100 Copper

EN 1.7379 steel belongs to the iron alloys classification, while C15100 copper belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.7379 steel and the bottom bar is C15100 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
120
Elongation at Break, % 21
2.0 to 36
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 74
43
Tensile Strength: Ultimate (UTS), MPa 670
260 to 470
Tensile Strength: Yield (Proof), MPa 460
69 to 460

Thermal Properties

Latent Heat of Fusion, J/g 260
210
Maximum Temperature: Mechanical, °C 460
200
Melting Completion (Liquidus), °C 1470
1100
Melting Onset (Solidus), °C 1420
1030
Specific Heat Capacity, J/kg-K 470
390
Thermal Conductivity, W/m-K 39
360
Thermal Expansion, µm/m-K 13
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
95
Electrical Conductivity: Equal Weight (Specific), % IACS 8.8
95

Otherwise Unclassified Properties

Base Metal Price, % relative 3.8
31
Density, g/cm3 7.8
9.0
Embodied Carbon, kg CO2/kg material 1.8
2.7
Embodied Energy, MJ/kg 23
43
Embodied Water, L/kg 59
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
9.3 to 71
Resilience: Unit (Modulus of Resilience), kJ/m3 550
21 to 890
Stiffness to Weight: Axial, points 13
7.2
Stiffness to Weight: Bending, points 24
18
Strength to Weight: Axial, points 24
8.1 to 15
Strength to Weight: Bending, points 22
10 to 15
Thermal Diffusivity, mm2/s 11
100
Thermal Shock Resistance, points 19
9.3 to 17

Alloy Composition

Carbon (C), % 0.13 to 0.2
0
Chromium (Cr), % 2.0 to 2.5
0
Copper (Cu), % 0
99.8 to 99.95
Iron (Fe), % 94.5 to 96.5
0
Manganese (Mn), % 0.5 to 0.9
0
Molybdenum (Mo), % 0.9 to 1.2
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.6
0
Sulfur (S), % 0 to 0.030
0
Zirconium (Zr), % 0
0.050 to 0.15
Residuals, % 0
0 to 0.1