EN 1.7383 Steel vs. S13800 Stainless Steel
Both EN 1.7383 steel and S13800 stainless steel are iron alloys. They have 79% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is EN 1.7383 steel and the bottom bar is S13800 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 170 to 180 | |
| 290 to 480 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 20 to 23 | |
| 11 to 18 |
| Fatigue Strength, MPa | 210 to 270 | |
| 410 to 870 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 74 | |
| 77 |
| Shear Strength, MPa | 350 to 380 | |
| 610 to 1030 |
| Tensile Strength: Ultimate (UTS), MPa | 560 to 610 | |
| 980 to 1730 |
| Tensile Strength: Yield (Proof), MPa | 300 to 400 | |
| 660 to 1580 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 460 | |
| 810 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1450 |
| Melting Onset (Solidus), °C | 1430 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 39 | |
| 16 |
| Thermal Expansion, µm/m-K | 13 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.7 | |
| 2.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.8 | |
| 2.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 3.9 | |
| 15 |
| Density, g/cm3 | 7.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.8 | |
| 3.4 |
| Embodied Energy, MJ/kg | 23 | |
| 46 |
| Embodied Water, L/kg | 59 | |
| 140 |
Common Calculations
| PREN (Pitting Resistance) | 5.6 | |
| 21 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
| 150 to 190 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 240 to 420 | |
| 1090 to 5490 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 20 to 22 | |
| 35 to 61 |
| Strength to Weight: Bending, points | 19 to 20 | |
| 28 to 41 |
| Thermal Diffusivity, mm2/s | 11 | |
| 4.3 |
| Thermal Shock Resistance, points | 16 to 18 | |
| 33 to 58 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.040 | |
| 0.9 to 1.4 |
| Carbon (C), % | 0.080 to 0.15 | |
| 0 to 0.050 |
| Chromium (Cr), % | 2.0 to 2.5 | |
| 12.3 to 13.2 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 |
| Iron (Fe), % | 94.3 to 96.6 | |
| 73.6 to 77.3 |
| Manganese (Mn), % | 0.4 to 0.8 | |
| 0 to 0.2 |
| Molybdenum (Mo), % | 0.9 to 1.1 | |
| 2.0 to 3.0 |
| Nickel (Ni), % | 0 to 0.3 | |
| 7.5 to 8.5 |
| Nitrogen (N), % | 0 | |
| 0 to 0.010 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.010 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.0080 |