EN 1.7386 Steel vs. AISI 205 Stainless Steel
Both EN 1.7386 steel and AISI 205 stainless steel are iron alloys. They have 75% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is EN 1.7386 steel and the bottom bar is AISI 205 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 170 to 200 | |
| 210 to 440 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 18 to 21 | |
| 11 to 51 |
| Fatigue Strength, MPa | 170 to 290 | |
| 410 to 640 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 75 | |
| 77 |
| Shear Strength, MPa | 340 to 410 | |
| 560 to 850 |
| Tensile Strength: Ultimate (UTS), MPa | 550 to 670 | |
| 800 to 1430 |
| Tensile Strength: Yield (Proof), MPa | 240 to 440 | |
| 450 to 1100 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 600 | |
| 880 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1380 |
| Melting Onset (Solidus), °C | 1410 | |
| 1340 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 480 |
| Thermal Expansion, µm/m-K | 13 | |
| 18 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 6.5 | |
| 11 |
| Density, g/cm3 | 7.8 | |
| 7.6 |
| Embodied Carbon, kg CO2/kg material | 2.0 | |
| 2.6 |
| Embodied Energy, MJ/kg | 28 | |
| 37 |
| Embodied Water, L/kg | 88 | |
| 150 |
Common Calculations
| PREN (Pitting Resistance) | 12 | |
| 23 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 92 to 110 | |
| 150 to 430 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 150 to 490 | |
| 510 to 3060 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 26 |
| Strength to Weight: Axial, points | 20 to 24 | |
| 29 to 52 |
| Strength to Weight: Bending, points | 19 to 22 | |
| 25 to 37 |
| Thermal Shock Resistance, points | 15 to 18 | |
| 16 to 29 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.040 | |
| 0 |
| Carbon (C), % | 0.080 to 0.15 | |
| 0.12 to 0.25 |
| Chromium (Cr), % | 8.0 to 10 | |
| 16.5 to 18.5 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 |
| Iron (Fe), % | 86.8 to 90.5 | |
| 62.6 to 68.1 |
| Manganese (Mn), % | 0.3 to 0.6 | |
| 14 to 15.5 |
| Molybdenum (Mo), % | 0.9 to 1.1 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 1.0 to 1.7 |
| Nitrogen (N), % | 0 | |
| 0.32 to 0.4 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.060 |
| Silicon (Si), % | 0.25 to 1.0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.030 |