EN 1.7386 Steel vs. ASTM B563 Pd-Ag-Cu
EN 1.7386 steel belongs to the iron alloys classification, while ASTM B563 Pd-Ag-Cu belongs to the otherwise unclassified metals. There are 19 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is EN 1.7386 steel and the bottom bar is ASTM B563 Pd-Ag-Cu.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 100 |
| Elongation at Break, % | 18 to 21 | |
| 7.0 to 17 |
| Poisson's Ratio | 0.28 | |
| 0.37 |
| Shear Modulus, GPa | 75 | |
| 37 |
| Shear Strength, MPa | 340 to 410 | |
| 470 to 690 |
| Tensile Strength: Ultimate (UTS), MPa | 550 to 670 | |
| 760 to 1170 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 150 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1180 |
| Melting Onset (Solidus), °C | 1410 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 260 |
| Thermal Expansion, µm/m-K | 13 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 9.0 | |
| 5.6 to 6.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 10 | |
| 4.6 to 5.5 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 11 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 5.2 |
| Stiffness to Weight: Bending, points | 25 | |
| 14 |
| Strength to Weight: Axial, points | 20 to 24 | |
| 19 to 30 |
| Strength to Weight: Bending, points | 19 to 22 | |
| 17 to 22 |
| Thermal Shock Resistance, points | 15 to 18 | |
| 39 to 61 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.040 | |
| 0 |
| Carbon (C), % | 0.080 to 0.15 | |
| 0 |
| Chromium (Cr), % | 8.0 to 10 | |
| 0 |
| Copper (Cu), % | 0 to 0.3 | |
| 15.5 to 16.5 |
| Iron (Fe), % | 86.8 to 90.5 | |
| 0 |
| Manganese (Mn), % | 0.3 to 0.6 | |
| 0 |
| Molybdenum (Mo), % | 0.9 to 1.1 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 0.8 to 1.2 |
| Palladium (Pd), % | 0 | |
| 43 to 45 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Platinum (Pt), % | 0 | |
| 0.8 to 1.2 |
| Silicon (Si), % | 0.25 to 1.0 | |
| 0 |
| Silver (Ag), % | 0 | |
| 37 to 39 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.4 |