EN 1.7386 Steel vs. EN 1.6368 Steel
Both EN 1.7386 steel and EN 1.6368 steel are iron alloys. They have a moderately high 90% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is EN 1.7386 steel and the bottom bar is EN 1.6368 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 170 to 200 | |
| 200 to 210 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 18 to 21 | |
| 18 |
| Fatigue Strength, MPa | 170 to 290 | |
| 310 to 330 |
| Impact Strength: V-Notched Charpy, J | 38 | |
| 43 to 46 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 75 | |
| 73 |
| Shear Strength, MPa | 340 to 410 | |
| 410 to 430 |
| Tensile Strength: Ultimate (UTS), MPa | 550 to 670 | |
| 660 to 690 |
| Tensile Strength: Yield (Proof), MPa | 240 to 440 | |
| 460 to 490 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 600 | |
| 410 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1460 |
| Melting Onset (Solidus), °C | 1410 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 26 | |
| 40 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 9.0 | |
| 7.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 10 | |
| 8.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 6.5 | |
| 3.4 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 2.0 | |
| 1.7 |
| Embodied Energy, MJ/kg | 28 | |
| 22 |
| Embodied Water, L/kg | 88 | |
| 53 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 92 to 110 | |
| 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 150 to 490 | |
| 580 to 650 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 20 to 24 | |
| 23 to 24 |
| Strength to Weight: Bending, points | 19 to 22 | |
| 21 to 22 |
| Thermal Diffusivity, mm2/s | 6.9 | |
| 11 |
| Thermal Shock Resistance, points | 15 to 18 | |
| 20 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.040 | |
| 0.015 to 0.040 |
| Carbon (C), % | 0.080 to 0.15 | |
| 0 to 0.17 |
| Chromium (Cr), % | 8.0 to 10 | |
| 0 to 0.3 |
| Copper (Cu), % | 0 to 0.3 | |
| 0.5 to 0.8 |
| Iron (Fe), % | 86.8 to 90.5 | |
| 95.1 to 97.2 |
| Manganese (Mn), % | 0.3 to 0.6 | |
| 0.8 to 1.2 |
| Molybdenum (Mo), % | 0.9 to 1.1 | |
| 0.25 to 0.5 |
| Nickel (Ni), % | 0 | |
| 1.0 to 1.3 |
| Niobium (Nb), % | 0 | |
| 0.015 to 0.045 |
| Nitrogen (N), % | 0 | |
| 0 to 0.020 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.025 |
| Silicon (Si), % | 0.25 to 1.0 | |
| 0.25 to 0.5 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.010 |