EN 1.7386 Steel vs. EN 1.7231 Steel
Both EN 1.7386 steel and EN 1.7231 steel are iron alloys. They have a moderately high 91% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is EN 1.7386 steel and the bottom bar is EN 1.7231 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 170 to 200 | |
| 240 to 280 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 18 to 21 | |
| 11 to 12 |
| Fatigue Strength, MPa | 170 to 290 | |
| 360 to 500 |
| Impact Strength: V-Notched Charpy, J | 38 | |
| 28 to 30 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 75 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 550 to 670 | |
| 790 to 930 |
| Tensile Strength: Yield (Proof), MPa | 240 to 440 | |
| 570 to 800 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 600 | |
| 420 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1460 |
| Melting Onset (Solidus), °C | 1410 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 26 | |
| 46 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 9.0 | |
| 7.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 10 | |
| 8.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 6.5 | |
| 2.5 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.0 | |
| 1.5 |
| Embodied Energy, MJ/kg | 28 | |
| 20 |
| Embodied Water, L/kg | 88 | |
| 51 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 92 to 110 | |
| 87 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 150 to 490 | |
| 870 to 1700 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 20 to 24 | |
| 28 to 33 |
| Strength to Weight: Bending, points | 19 to 22 | |
| 24 to 27 |
| Thermal Diffusivity, mm2/s | 6.9 | |
| 12 |
| Thermal Shock Resistance, points | 15 to 18 | |
| 23 to 27 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.040 | |
| 0 |
| Carbon (C), % | 0.080 to 0.15 | |
| 0.38 to 0.45 |
| Chromium (Cr), % | 8.0 to 10 | |
| 0.8 to 1.2 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 |
| Iron (Fe), % | 86.8 to 90.5 | |
| 96.4 to 98.1 |
| Manganese (Mn), % | 0.3 to 0.6 | |
| 0.6 to 1.0 |
| Molybdenum (Mo), % | 0.9 to 1.1 | |
| 0.15 to 0.3 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.025 |
| Silicon (Si), % | 0.25 to 1.0 | |
| 0 to 0.6 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.030 |