EN 1.7701 Steel vs. SAE-AISI 5160 Steel
Both EN 1.7701 steel and SAE-AISI 5160 steel are iron alloys. Their average alloy composition is basically identical. There are 25 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is EN 1.7701 steel and the bottom bar is SAE-AISI 5160 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 200 to 480 | |
| 200 to 340 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 670 to 2010 | |
| 660 to 1150 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 420 | |
| 420 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1450 |
| Melting Onset (Solidus), °C | 1420 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 44 | |
| 43 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.4 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.5 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.6 | |
| 2.1 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.9 | |
| 1.4 |
| Embodied Energy, MJ/kg | 26 | |
| 19 |
| Embodied Water, L/kg | 52 | |
| 50 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 24 to 71 | |
| 23 to 41 |
| Strength to Weight: Bending, points | 22 to 45 | |
| 22 to 31 |
| Thermal Diffusivity, mm2/s | 12 | |
| 12 |
| Thermal Shock Resistance, points | 20 to 59 | |
| 19 to 34 |
Alloy Composition
| Carbon (C), % | 0.48 to 0.56 | |
| 0.56 to 0.61 |
| Chromium (Cr), % | 0.9 to 1.2 | |
| 0.7 to 0.9 |
| Iron (Fe), % | 96.2 to 97.7 | |
| 97.1 to 97.8 |
| Manganese (Mn), % | 0.7 to 1.1 | |
| 0.75 to 1.0 |
| Molybdenum (Mo), % | 0.15 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 to 0.4 | |
| 0.15 to 0.35 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.040 |
| Vanadium (V), % | 0.1 to 0.2 | |
| 0 |