EN 1.7703 Steel vs. Solder Alloy 103

EN 1.7703 steel belongs to the iron alloys classification, while solder alloy 103 belongs to the otherwise unclassified metals. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.7703 steel and the bottom bar is solder alloy 103.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
37
Elongation at Break, % 20
47
Poisson's Ratio 0.29
0.39
Shear Modulus, GPa 74
13
Tensile Strength: Ultimate (UTS), MPa 670 to 690
52

Thermal Properties

Latent Heat of Fusion, J/g 250
45
Melting Completion (Liquidus), °C 1470
190
Melting Onset (Solidus), °C 1430
180
Specific Heat Capacity, J/kg-K 470
180
Thermal Conductivity, W/m-K 39
50
Thermal Expansion, µm/m-K 13
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
11
Electrical Conductivity: Equal Weight (Specific), % IACS 8.7
12

Otherwise Unclassified Properties

Density, g/cm3 7.9
8.9
Embodied Carbon, kg CO2/kg material 2.5
10
Embodied Energy, MJ/kg 35
180
Embodied Water, L/kg 61
910

Common Calculations

Stiffness to Weight: Axial, points 13
2.3
Stiffness to Weight: Bending, points 24
12
Strength to Weight: Axial, points 24
1.6
Strength to Weight: Bending, points 22
3.5
Thermal Diffusivity, mm2/s 11
30
Thermal Shock Resistance, points 19 to 20
4.3

Alloy Composition

Aluminum (Al), % 0
0 to 0.0010
Antimony (Sb), % 0
0 to 0.2
Arsenic (As), % 0
0 to 0.030
Bismuth (Bi), % 0
0 to 0.1
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0.11 to 0.15
0
Chromium (Cr), % 2.0 to 2.5
0
Copper (Cu), % 0 to 0.2
0 to 0.080
Gold (Au), % 0
0 to 0.050
Indium (In), % 0
0 to 0.1
Iron (Fe), % 94.6 to 96.4
0 to 0.020
Lead (Pb), % 0
38.8 to 40.5
Manganese (Mn), % 0.3 to 0.6
0
Molybdenum (Mo), % 0.9 to 1.1
0
Nickel (Ni), % 0 to 0.25
0 to 0.010
Niobium (Nb), % 0 to 0.070
0
Nitrogen (N), % 0 to 0.012
0
Phosphorus (P), % 0 to 0.015
0
Silicon (Si), % 0 to 0.1
0
Silver (Ag), % 0
0 to 0.1
Sulfur (S), % 0 to 0.0050
0
Tin (Sn), % 0
59.5 to 60.5
Titanium (Ti), % 0 to 0.030
0
Vanadium (V), % 0.25 to 0.35
0
Zinc (Zn), % 0
0 to 0.0010