EN 1.7706 Steel vs. EN 1.7338 Steel

Both EN 1.7706 steel and EN 1.7338 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.7706 steel and the bottom bar is EN 1.7338 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
150
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 17
23
Fatigue Strength, MPa 330
220
Impact Strength: V-Notched Charpy, J 30
38
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 690
490
Tensile Strength: Yield (Proof), MPa 500
300

Thermal Properties

Latent Heat of Fusion, J/g 260
260
Maximum Temperature: Mechanical, °C 440
430
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
40
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 8.7
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 3.7
3.1
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 2.3
1.6
Embodied Energy, MJ/kg 32
21
Embodied Water, L/kg 57
53

Common Calculations

PREN (Pitting Resistance) 4.7
3.1
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
97
Resilience: Unit (Modulus of Resilience), kJ/m3 670
240
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 24
17
Strength to Weight: Bending, points 22
18
Thermal Diffusivity, mm2/s 11
11
Thermal Shock Resistance, points 20
14

Alloy Composition

Aluminum (Al), % 0
0 to 0.040
Carbon (C), % 0.15 to 0.2
0 to 0.15
Chromium (Cr), % 1.2 to 1.5
1.0 to 1.5
Copper (Cu), % 0 to 0.3
0 to 0.3
Iron (Fe), % 94.7 to 97.1
95.4 to 97.8
Manganese (Mn), % 0.5 to 0.9
0.3 to 0.6
Molybdenum (Mo), % 0.9 to 1.1
0.45 to 0.65
Nickel (Ni), % 0 to 0.4
0 to 0.3
Phosphorus (P), % 0 to 0.020
0 to 0.025
Silicon (Si), % 0 to 0.6
0.5 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.010
Vanadium (V), % 0.2 to 0.3
0