EN 1.7709 Steel vs. AWS E2593
Both EN 1.7709 steel and AWS E2593 are iron alloys. They have 61% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is EN 1.7709 steel and the bottom bar is AWS E2593.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Poisson's Ratio | 0.29 | |
| 0.27 |
| Shear Modulus, GPa | 73 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 650 to 780 | |
| 850 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 300 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1430 |
| Melting Onset (Solidus), °C | 1420 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 33 | |
| 16 |
| Thermal Expansion, µm/m-K | 11 | |
| 14 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 3.4 | |
| 22 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.3 | |
| 4.2 |
| Embodied Energy, MJ/kg | 32 | |
| 59 |
| Embodied Water, L/kg | 56 | |
| 190 |
Common Calculations
| PREN (Pitting Resistance) | 3.6 | |
| 39 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 23 to 27 | |
| 30 |
| Strength to Weight: Bending, points | 21 to 24 | |
| 25 |
| Thermal Diffusivity, mm2/s | 8.9 | |
| 4.3 |
| Thermal Shock Resistance, points | 22 to 26 | |
| 21 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.030 | |
| 0 |
| Carbon (C), % | 0.17 to 0.25 | |
| 0 to 0.040 |
| Chromium (Cr), % | 1.2 to 1.5 | |
| 24 to 27 |
| Copper (Cu), % | 0 | |
| 1.5 to 3.0 |
| Iron (Fe), % | 95.2 to 97.5 | |
| 52.7 to 62.5 |
| Manganese (Mn), % | 0.4 to 0.8 | |
| 0.5 to 1.5 |
| Molybdenum (Mo), % | 0.55 to 0.8 | |
| 2.9 to 3.9 |
| Nickel (Ni), % | 0 to 0.6 | |
| 8.5 to 10.5 |
| Nitrogen (N), % | 0 | |
| 0.080 to 0.25 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Vanadium (V), % | 0.2 to 0.35 | |
| 0 |