EN 1.7709 Steel vs. S30601 Stainless Steel

Both EN 1.7709 steel and S30601 stainless steel are iron alloys. They have 61% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is EN 1.7709 steel and the bottom bar is S30601 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 230
190
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
75
Tensile Strength: Ultimate (UTS), MPa 650 to 780
660

Thermal Properties

Latent Heat of Fusion, J/g 250
370
Maximum Temperature: Mechanical, °C 440
950
Melting Completion (Liquidus), °C 1470
1360
Melting Onset (Solidus), °C 1420
1310
Specific Heat Capacity, J/kg-K 470
500
Thermal Expansion, µm/m-K 11
15

Otherwise Unclassified Properties

Base Metal Price, % relative 3.4
20
Density, g/cm3 7.8
7.6
Embodied Carbon, kg CO2/kg material 2.3
3.9
Embodied Energy, MJ/kg 32
55
Embodied Water, L/kg 56
150

Common Calculations

PREN (Pitting Resistance) 3.6
18
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 23 to 27
24
Strength to Weight: Bending, points 21 to 24
22
Thermal Shock Resistance, points 22 to 26
16

Alloy Composition

Aluminum (Al), % 0 to 0.030
0
Carbon (C), % 0.17 to 0.25
0 to 0.015
Chromium (Cr), % 1.2 to 1.5
17 to 18
Copper (Cu), % 0
0 to 0.35
Iron (Fe), % 95.2 to 97.5
56.9 to 60.5
Manganese (Mn), % 0.4 to 0.8
0.5 to 0.8
Molybdenum (Mo), % 0.55 to 0.8
0 to 0.2
Nickel (Ni), % 0 to 0.6
17 to 18
Nitrogen (N), % 0
0 to 0.050
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 0 to 0.4
5.0 to 5.6
Sulfur (S), % 0 to 0.030
0 to 0.013
Vanadium (V), % 0.2 to 0.35
0