EN 1.7711 Steel vs. EN 1.4931 Steel

Both EN 1.7711 steel and EN 1.4931 steel are iron alloys. They have 88% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.7711 steel and the bottom bar is EN 1.4931 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210 to 280
240
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 16 to 22
17
Fatigue Strength, MPa 290 to 520
410
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Tensile Strength: Ultimate (UTS), MPa 690 to 930
810
Tensile Strength: Yield (Proof), MPa 400 to 800
620

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Maximum Temperature: Mechanical, °C 430
600
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 33
24
Thermal Expansion, µm/m-K 11
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
9.8
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
11

Otherwise Unclassified Properties

Base Metal Price, % relative 3.0
8.5
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.3
2.9
Embodied Energy, MJ/kg 32
42
Embodied Water, L/kg 54
100

Common Calculations

PREN (Pitting Resistance) 2.9
16
Resilience: Ultimate (Unit Rupture Work), MJ/m3 130 to 140
130
Resilience: Unit (Modulus of Resilience), kJ/m3 430 to 1690
970
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 24 to 33
29
Strength to Weight: Bending, points 22 to 27
25
Thermal Diffusivity, mm2/s 8.9
6.5
Thermal Shock Resistance, points 24 to 32
22

Alloy Composition

Aluminum (Al), % 0 to 0.015
0
Carbon (C), % 0.36 to 0.44
0.2 to 0.26
Chromium (Cr), % 0.9 to 1.2
11.3 to 12.2
Iron (Fe), % 96 to 97.5
83.2 to 86.8
Manganese (Mn), % 0.45 to 0.85
0.5 to 0.8
Molybdenum (Mo), % 0.5 to 0.65
1.0 to 1.2
Nickel (Ni), % 0
0 to 1.0
Phosphorus (P), % 0 to 0.025
0 to 0.030
Silicon (Si), % 0 to 0.4
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.020
Tungsten (W), % 0
0 to 0.5
Vanadium (V), % 0.25 to 0.35
0.25 to 0.35