EN 1.7711 steel belongs to the iron alloys classification, while ZA-12 belongs to the zinc alloys. There are 31 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is EN 1.7711 steel and the bottom bar is ZA-12.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 210 to 280 | |
89 to 100 |
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
83 |
Elongation at Break, % | 16 to 22 | |
1.6 to 5.3 |
Fatigue Strength, MPa | 290 to 520 | |
73 to 120 |
Poisson's Ratio | 0.29 | |
0.26 |
Shear Modulus, GPa | 73 | |
33 |
Shear Strength, MPa | 440 to 570 | |
240 to 300 |
Tensile Strength: Ultimate (UTS), MPa | 690 to 930 | |
260 to 400 |
Tensile Strength: Yield (Proof), MPa | 400 to 800 | |
210 to 320 |
Thermal Properties
Latent Heat of Fusion, J/g | 250 | |
120 |
Maximum Temperature: Mechanical, °C | 430 | |
100 |
Melting Completion (Liquidus), °C | 1460 | |
430 |
Melting Onset (Solidus), °C | 1420 | |
380 |
Specific Heat Capacity, J/kg-K | 470 | |
450 |
Thermal Conductivity, W/m-K | 33 | |
120 |
Thermal Expansion, µm/m-K | 11 | |
24 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 7.4 | |
28 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 8.5 | |
42 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 3.0 | |
11 |
Density, g/cm3 | 7.8 | |
6.0 |
Embodied Carbon, kg CO2/kg material | 2.3 | |
3.4 |
Embodied Energy, MJ/kg | 32 | |
64 |
Embodied Water, L/kg | 54 | |
440 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 130 to 140 | |
4.0 to 20 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 430 to 1690 | |
260 to 620 |
Stiffness to Weight: Axial, points | 13 | |
7.6 |
Stiffness to Weight: Bending, points | 24 | |
24 |
Strength to Weight: Axial, points | 24 to 33 | |
12 to 19 |
Strength to Weight: Bending, points | 22 to 27 | |
15 to 20 |
Thermal Diffusivity, mm2/s | 8.9 | |
43 |
Thermal Shock Resistance, points | 24 to 32 | |
9.4 to 14 |
Alloy Composition
Aluminum (Al), % | 0 to 0.015 | |
10.5 to 11.5 |
Cadmium (Cd), % | 0 | |
0 to 0.0060 |
Carbon (C), % | 0.36 to 0.44 | |
0 |
Chromium (Cr), % | 0.9 to 1.2 | |
0 |
Copper (Cu), % | 0 | |
0.5 to 1.2 |
Iron (Fe), % | 96 to 97.5 | |
0 to 0.075 |
Lead (Pb), % | 0 | |
0 to 0.0060 |
Magnesium (Mg), % | 0 | |
0.015 to 0.030 |
Manganese (Mn), % | 0.45 to 0.85 | |
0 |
Molybdenum (Mo), % | 0.5 to 0.65 | |
0 |
Nickel (Ni), % | 0 | |
0 to 0.020 |
Phosphorus (P), % | 0 to 0.025 | |
0 |
Silicon (Si), % | 0 to 0.4 | |
0 to 0.060 |
Sulfur (S), % | 0 to 0.030 | |
0 |
Tin (Sn), % | 0 | |
0 to 0.0030 |
Vanadium (V), % | 0.25 to 0.35 | |
0 |
Zinc (Zn), % | 0 | |
87.1 to 89 |