EN 1.7715 Steel vs. ASTM A182 Grade F92

Both EN 1.7715 steel and ASTM A182 grade F92 are iron alloys. Both are furnished in the normalized and tempered condition. They have 90% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.7715 steel and the bottom bar is ASTM A182 grade F92.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
240
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 21
22
Fatigue Strength, MPa 240
360
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Shear Strength, MPa 340
440
Tensile Strength: Ultimate (UTS), MPa 540
690
Tensile Strength: Yield (Proof), MPa 340
500

Thermal Properties

Latent Heat of Fusion, J/g 250
260
Maximum Temperature: Mechanical, °C 420
590
Melting Completion (Liquidus), °C 1470
1490
Melting Onset (Solidus), °C 1430
1450
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
26
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
9.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
10

Otherwise Unclassified Properties

Base Metal Price, % relative 2.9
11
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 2.2
2.8
Embodied Energy, MJ/kg 30
40
Embodied Water, L/kg 52
89

Common Calculations

PREN (Pitting Resistance) 2.4
14
Resilience: Ultimate (Unit Rupture Work), MJ/m3 99
140
Resilience: Unit (Modulus of Resilience), kJ/m3 320
650
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19
24
Strength to Weight: Bending, points 19
22
Thermal Diffusivity, mm2/s 11
6.9
Thermal Shock Resistance, points 16
19

Alloy Composition

Aluminum (Al), % 0 to 0.040
0 to 0.020
Boron (B), % 0
0.0010 to 0.0060
Carbon (C), % 0.1 to 0.15
0.070 to 0.13
Chromium (Cr), % 0.3 to 0.6
8.5 to 9.5
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 96.5 to 98.3
85.8 to 89.1
Manganese (Mn), % 0.4 to 0.7
0.3 to 0.6
Molybdenum (Mo), % 0.5 to 0.7
0.3 to 0.6
Nickel (Ni), % 0 to 0.3
0 to 0.4
Niobium (Nb), % 0
0.040 to 0.090
Nitrogen (N), % 0
0.030 to 0.070
Phosphorus (P), % 0 to 0.025
0 to 0.020
Silicon (Si), % 0.15 to 0.35
0 to 0.5
Sulfur (S), % 0 to 0.010
0 to 0.010
Titanium (Ti), % 0
0 to 0.010
Tungsten (W), % 0
1.5 to 2.0
Vanadium (V), % 0.22 to 0.28
0.15 to 0.25
Zirconium (Zr), % 0
0 to 0.010