EN 1.7715 Steel vs. EN 1.4634 Stainless Steel

Both EN 1.7715 steel and EN 1.4634 stainless steel are iron alloys. They have 80% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.7715 steel and the bottom bar is EN 1.4634 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 21
21
Fatigue Strength, MPa 240
180
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Shear Strength, MPa 340
340
Tensile Strength: Ultimate (UTS), MPa 540
540
Tensile Strength: Yield (Proof), MPa 340
280

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 420
900
Melting Completion (Liquidus), °C 1470
1430
Melting Onset (Solidus), °C 1430
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 40
21
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
3.0

Otherwise Unclassified Properties

Base Metal Price, % relative 2.9
13
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 2.2
2.9
Embodied Energy, MJ/kg 30
42
Embodied Water, L/kg 52
140

Common Calculations

PREN (Pitting Resistance) 2.4
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 99
93
Resilience: Unit (Modulus of Resilience), kJ/m3 320
200
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
20
Strength to Weight: Bending, points 19
19
Thermal Diffusivity, mm2/s 11
5.8
Thermal Shock Resistance, points 16
19

Alloy Composition

Aluminum (Al), % 0 to 0.040
0.2 to 1.5
Carbon (C), % 0.1 to 0.15
0 to 0.030
Chromium (Cr), % 0.3 to 0.6
17.5 to 18.5
Copper (Cu), % 0 to 0.3
0 to 0.5
Iron (Fe), % 96.5 to 98.3
74.9 to 81.8
Manganese (Mn), % 0.4 to 0.7
0 to 1.0
Molybdenum (Mo), % 0.5 to 0.7
0 to 0.5
Nickel (Ni), % 0 to 0.3
0 to 0.5
Niobium (Nb), % 0
0.3 to 1.0
Phosphorus (P), % 0 to 0.025
0 to 0.050
Silicon (Si), % 0.15 to 0.35
0.2 to 1.5
Sulfur (S), % 0 to 0.010
0 to 0.050
Vanadium (V), % 0.22 to 0.28
0