EN 1.7715 Steel vs. SAE-AISI 1137 Steel

Both EN 1.7715 steel and SAE-AISI 1137 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.7715 steel and the bottom bar is SAE-AISI 1137 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
200 to 210
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 21
11 to 17
Fatigue Strength, MPa 240
250 to 400
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 340
430 to 460
Tensile Strength: Ultimate (UTS), MPa 540
700 to 760
Tensile Strength: Yield (Proof), MPa 340
370 to 650

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 420
400
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
51
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
10
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
12

Otherwise Unclassified Properties

Base Metal Price, % relative 2.9
1.9
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 2.2
1.4
Embodied Energy, MJ/kg 30
19
Embodied Water, L/kg 52
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 99
81 to 100
Resilience: Unit (Modulus of Resilience), kJ/m3 320
360 to 1130
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19
25 to 27
Strength to Weight: Bending, points 19
22 to 24
Thermal Diffusivity, mm2/s 11
14
Thermal Shock Resistance, points 16
21 to 23

Alloy Composition

Aluminum (Al), % 0 to 0.040
0
Carbon (C), % 0.1 to 0.15
0.32 to 0.39
Chromium (Cr), % 0.3 to 0.6
0
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 96.5 to 98.3
97.8 to 98.3
Manganese (Mn), % 0.4 to 0.7
1.4 to 1.7
Molybdenum (Mo), % 0.5 to 0.7
0
Nickel (Ni), % 0 to 0.3
0
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0.15 to 0.35
0
Sulfur (S), % 0 to 0.010
0.080 to 0.13
Vanadium (V), % 0.22 to 0.28
0