EN 1.7720 Steel vs. EN 1.5535 Steel

Both EN 1.7720 steel and EN 1.5535 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.7720 steel and the bottom bar is EN 1.5535 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
130 to 180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 19
11 to 22
Fatigue Strength, MPa 230
210 to 320
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 590
450 to 1490
Tensile Strength: Yield (Proof), MPa 340
300 to 500

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 410
400
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
50
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 2.8
1.9
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 2.2
1.4
Embodied Energy, MJ/kg 30
19
Embodied Water, L/kg 51
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 97
45 to 250
Resilience: Unit (Modulus of Resilience), kJ/m3 300
240 to 680
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 21
16 to 53
Strength to Weight: Bending, points 20
17 to 37
Thermal Diffusivity, mm2/s 11
13
Thermal Shock Resistance, points 17
13 to 44

Alloy Composition

Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0.1 to 0.15
0.2 to 0.25
Chromium (Cr), % 0.3 to 0.5
0 to 0.3
Copper (Cu), % 0 to 0.3
0 to 0.25
Iron (Fe), % 96.6 to 98.6
97.6 to 98.9
Manganese (Mn), % 0.4 to 0.7
0.9 to 1.2
Molybdenum (Mo), % 0.4 to 0.6
0
Nickel (Ni), % 0 to 0.4
0
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 0.45
0 to 0.3
Sulfur (S), % 0 to 0.020
0 to 0.025
Vanadium (V), % 0.22 to 0.3
0