EN 1.7725 Steel vs. S32202 Stainless Steel

Both EN 1.7725 steel and S32202 stainless steel are iron alloys. They have 76% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.7725 steel and the bottom bar is S32202 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 250 to 300
250
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 14
34
Fatigue Strength, MPa 390 to 550
400
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
79
Tensile Strength: Ultimate (UTS), MPa 830 to 1000
730
Tensile Strength: Yield (Proof), MPa 610 to 860
510

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 440
1030
Melting Completion (Liquidus), °C 1460
1430
Melting Onset (Solidus), °C 1420
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 39
15
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.9
12
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.8
2.6
Embodied Energy, MJ/kg 24
37
Embodied Water, L/kg 54
150

Common Calculations

PREN (Pitting Resistance) 2.8
27
Resilience: Ultimate (Unit Rupture Work), MJ/m3 110 to 130
220
Resilience: Unit (Modulus of Resilience), kJ/m3 980 to 1940
650
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 29 to 35
27
Strength to Weight: Bending, points 25 to 28
24
Thermal Diffusivity, mm2/s 11
4.0
Thermal Shock Resistance, points 24 to 29
20

Alloy Composition

Carbon (C), % 0.27 to 0.34
0 to 0.030
Chromium (Cr), % 1.3 to 1.7
21.5 to 24
Iron (Fe), % 95.7 to 97.5
69.4 to 77.3
Manganese (Mn), % 0.6 to 1.0
0 to 2.0
Molybdenum (Mo), % 0.3 to 0.5
0 to 0.45
Nickel (Ni), % 0
1.0 to 2.8
Nitrogen (N), % 0
0.18 to 0.26
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.6
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.010
Vanadium (V), % 0.050 to 0.15
0