EN 1.7729 Steel vs. ASTM A369 Grade FPB

Both EN 1.7729 steel and ASTM A369 grade FPB are iron alloys. They have a very high 97% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.7729 steel and the bottom bar is ASTM A369 grade FPB.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 270
140
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 17
19
Fatigue Strength, MPa 500
180
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 560
290
Tensile Strength: Ultimate (UTS), MPa 910
470
Tensile Strength: Yield (Proof), MPa 750
270

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 430
400
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
52
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.7
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 3.8
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.3
1.4
Embodied Energy, MJ/kg 49
18
Embodied Water, L/kg 59
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
78
Resilience: Unit (Modulus of Resilience), kJ/m3 1500
190
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 32
17
Strength to Weight: Bending, points 27
17
Thermal Diffusivity, mm2/s 11
14
Thermal Shock Resistance, points 27
15

Alloy Composition

Aluminum (Al), % 0.015 to 0.080
0
Arsenic (As), % 0 to 0.020
0
Boron (B), % 0.0010 to 0.010
0
Carbon (C), % 0.17 to 0.23
0 to 0.3
Chromium (Cr), % 0.9 to 1.2
0
Copper (Cu), % 0 to 0.2
0
Iron (Fe), % 94.8 to 97
98.1 to 99.61
Manganese (Mn), % 0.35 to 0.75
0.29 to 1.1
Molybdenum (Mo), % 0.9 to 1.1
0
Nickel (Ni), % 0 to 0.2
0
Phosphorus (P), % 0 to 0.020
0 to 0.035
Silicon (Si), % 0 to 0.4
0.1 to 0.5
Sulfur (S), % 0 to 0.015
0 to 0.035
Tin (Sn), % 0 to 0.020
0
Titanium (Ti), % 0.070 to 0.15
0
Vanadium (V), % 0.6 to 0.8
0