MakeItFrom.com
Menu (ESC)

EN 1.7729 Steel vs. SAE-AISI M3 Class 2 Steel

Both EN 1.7729 steel and SAE-AISI M3 class 2 steel are iron alloys. They have 83% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is EN 1.7729 steel and the bottom bar is SAE-AISI M3 class 2 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
77
Tensile Strength: Ultimate (UTS), MPa 910
770 to 2210

Thermal Properties

Latent Heat of Fusion, J/g 250
260
Melting Completion (Liquidus), °C 1470
1620
Melting Onset (Solidus), °C 1430
1570
Specific Heat Capacity, J/kg-K 470
440
Thermal Conductivity, W/m-K 40
26
Thermal Expansion, µm/m-K 13
12

Otherwise Unclassified Properties

Base Metal Price, % relative 3.8
25
Density, g/cm3 7.8
8.3
Embodied Carbon, kg CO2/kg material 3.3
12
Embodied Energy, MJ/kg 49
180
Embodied Water, L/kg 59
110

Common Calculations

PREN (Pitting Resistance) 4.4
33
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 32
26 to 74
Strength to Weight: Bending, points 27
22 to 45
Thermal Diffusivity, mm2/s 11
7.2
Thermal Shock Resistance, points 27
24 to 69

Alloy Composition

Aluminum (Al), % 0.015 to 0.080
0
Arsenic (As), % 0 to 0.020
0
Boron (B), % 0.0010 to 0.010
0
Carbon (C), % 0.17 to 0.23
1.2 to 1.3
Chromium (Cr), % 0.9 to 1.2
3.8 to 4.5
Copper (Cu), % 0 to 0.2
0 to 0.25
Iron (Fe), % 94.8 to 97
75.8 to 82.3
Manganese (Mn), % 0.35 to 0.75
0.15 to 0.4
Molybdenum (Mo), % 0.9 to 1.1
4.8 to 6.5
Nickel (Ni), % 0 to 0.2
0 to 0.3
Phosphorus (P), % 0 to 0.020
0 to 0.030
Silicon (Si), % 0 to 0.4
0.2 to 0.45
Sulfur (S), % 0 to 0.015
0 to 0.030
Tin (Sn), % 0 to 0.020
0
Titanium (Ti), % 0.070 to 0.15
0
Tungsten (W), % 0
5.0 to 6.8
Vanadium (V), % 0.6 to 0.8
2.8 to 3.8