EN 1.7767 Steel vs. AISI 422 Stainless Steel

Both EN 1.7767 steel and AISI 422 stainless steel are iron alloys. They have 89% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.7767 steel and the bottom bar is AISI 422 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 210
260 to 330
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 20
15 to 17
Fatigue Strength, MPa 320 to 340
410 to 500
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
76
Shear Strength, MPa 420 to 430
560 to 660
Tensile Strength: Ultimate (UTS), MPa 670 to 690
910 to 1080
Tensile Strength: Yield (Proof), MPa 460 to 500
670 to 870

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Maximum Temperature: Mechanical, °C 480
650
Melting Completion (Liquidus), °C 1470
1480
Melting Onset (Solidus), °C 1430
1470
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
24
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.7
4.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
5.3

Otherwise Unclassified Properties

Base Metal Price, % relative 4.5
11
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 2.4
3.1
Embodied Energy, MJ/kg 33
44
Embodied Water, L/kg 64
100

Common Calculations

PREN (Pitting Resistance) 6.4
17
Resilience: Ultimate (Unit Rupture Work), MJ/m3 120 to 130
140 to 150
Resilience: Unit (Modulus of Resilience), kJ/m3 570 to 650
1140 to 1910
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 24
32 to 38
Strength to Weight: Bending, points 22
26 to 30
Thermal Diffusivity, mm2/s 11
6.4
Thermal Shock Resistance, points 19 to 20
33 to 39

Alloy Composition

Carbon (C), % 0.1 to 0.15
0.2 to 0.25
Chromium (Cr), % 2.8 to 3.3
11 to 12.5
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 93.8 to 95.8
81.9 to 85.8
Manganese (Mn), % 0.3 to 0.6
0.5 to 1.0
Molybdenum (Mo), % 0.9 to 1.1
0.9 to 1.3
Nickel (Ni), % 0 to 0.25
0.5 to 1.0
Niobium (Nb), % 0 to 0.070
0
Nitrogen (N), % 0 to 0.012
0
Phosphorus (P), % 0 to 0.015
0 to 0.025
Silicon (Si), % 0 to 0.15
0 to 0.5
Sulfur (S), % 0 to 0.0050
0 to 0.025
Titanium (Ti), % 0 to 0.030
0
Tungsten (W), % 0
0.9 to 1.3
Vanadium (V), % 0.2 to 0.3
0.2 to 0.3