EN 1.7767 Steel vs. EN 1.7336 Steel
Both EN 1.7767 steel and EN 1.7336 steel are iron alloys. They have a very high 97% of their average alloy composition in common.
For each property being compared, the top bar is EN 1.7767 steel and the bottom bar is EN 1.7336 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 200 to 210 | |
| 180 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 20 | |
| 22 |
| Fatigue Strength, MPa | 320 to 340 | |
| 240 to 310 |
| Impact Strength: V-Notched Charpy, J | 46 | |
| 39 to 46 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 74 | |
| 73 |
| Shear Strength, MPa | 420 to 430 | |
| 370 |
| Tensile Strength: Ultimate (UTS), MPa | 670 to 690 | |
| 590 |
| Tensile Strength: Yield (Proof), MPa | 460 to 500 | |
| 340 to 440 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 480 | |
| 430 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1460 |
| Melting Onset (Solidus), °C | 1430 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 40 | |
| 40 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.7 | |
| 7.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.9 | |
| 8.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 4.5 | |
| 3.1 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.4 | |
| 1.6 |
| Embodied Energy, MJ/kg | 33 | |
| 21 |
| Embodied Water, L/kg | 64 | |
| 53 |
Common Calculations
| PREN (Pitting Resistance) | 6.4 | |
| 3.2 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 120 to 130 | |
| 110 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 570 to 650 | |
| 310 to 510 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 24 | |
| 21 |
| Strength to Weight: Bending, points | 22 | |
| 20 |
| Thermal Diffusivity, mm2/s | 11 | |
| 11 |
| Thermal Shock Resistance, points | 19 to 20 | |
| 17 |
Alloy Composition
| Carbon (C), % | 0.1 to 0.15 | |
| 0 to 0.17 |
| Chromium (Cr), % | 2.8 to 3.3 | |
| 1.0 to 1.5 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 0.3 |
| Iron (Fe), % | 93.8 to 95.8 | |
| 95.6 to 97.7 |
| Manganese (Mn), % | 0.3 to 0.6 | |
| 0.4 to 0.65 |
| Molybdenum (Mo), % | 0.9 to 1.1 | |
| 0.45 to 0.65 |
| Nickel (Ni), % | 0 to 0.25 | |
| 0 to 0.3 |
| Niobium (Nb), % | 0 to 0.070 | |
| 0 |
| Nitrogen (N), % | 0 to 0.012 | |
| 0 to 0.012 |
| Phosphorus (P), % | 0 to 0.015 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 to 0.15 | |
| 0.5 to 0.8 |
| Sulfur (S), % | 0 to 0.0050 | |
| 0 to 0.0050 |
| Titanium (Ti), % | 0 to 0.030 | |
| 0 |
| Vanadium (V), % | 0.2 to 0.3 | |
| 0 |