EN 1.7767 Steel vs. S35000 Stainless Steel

Both EN 1.7767 steel and S35000 stainless steel are iron alloys. They have 80% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.7767 steel and the bottom bar is S35000 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 20
2.3 to 14
Fatigue Strength, MPa 320 to 340
380 to 520
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
78
Shear Strength, MPa 420 to 430
740 to 950
Tensile Strength: Ultimate (UTS), MPa 670 to 690
1300 to 1570
Tensile Strength: Yield (Proof), MPa 460 to 500
660 to 1160

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 480
900
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
16
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.7
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 4.5
14
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 2.4
3.2
Embodied Energy, MJ/kg 33
44
Embodied Water, L/kg 64
130

Common Calculations

PREN (Pitting Resistance) 6.4
28
Resilience: Ultimate (Unit Rupture Work), MJ/m3 120 to 130
28 to 170
Resilience: Unit (Modulus of Resilience), kJ/m3 570 to 650
1070 to 3360
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 24
46 to 56
Strength to Weight: Bending, points 22
34 to 38
Thermal Diffusivity, mm2/s 11
4.4
Thermal Shock Resistance, points 19 to 20
42 to 51

Alloy Composition

Carbon (C), % 0.1 to 0.15
0.070 to 0.11
Chromium (Cr), % 2.8 to 3.3
16 to 17
Copper (Cu), % 0 to 0.25
0
Iron (Fe), % 93.8 to 95.8
72.7 to 76.9
Manganese (Mn), % 0.3 to 0.6
0.5 to 1.3
Molybdenum (Mo), % 0.9 to 1.1
2.5 to 3.2
Nickel (Ni), % 0 to 0.25
4.0 to 5.0
Niobium (Nb), % 0 to 0.070
0
Nitrogen (N), % 0 to 0.012
0.070 to 0.13
Phosphorus (P), % 0 to 0.015
0 to 0.040
Silicon (Si), % 0 to 0.15
0 to 0.5
Sulfur (S), % 0 to 0.0050
0 to 0.030
Titanium (Ti), % 0 to 0.030
0
Vanadium (V), % 0.2 to 0.3
0