EN 1.7779 Steel vs. EN 1.5414 Steel

Both EN 1.7779 steel and EN 1.5414 steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.7779 steel and the bottom bar is EN 1.5414 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 240
170 to 180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 16
22
Fatigue Strength, MPa 430
250 to 270
Impact Strength: V-Notched Charpy, J 38
46
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 500
350 to 370
Tensile Strength: Ultimate (UTS), MPa 810
550 to 580
Tensile Strength: Yield (Proof), MPa 660
350 to 380

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 470
410
Melting Completion (Liquidus), °C 1460
1470
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
44
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.7
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 4.0
2.6
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.8
1.6
Embodied Energy, MJ/kg 41
21
Embodied Water, L/kg 64
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
110
Resilience: Unit (Modulus of Resilience), kJ/m3 1150
320 to 370
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 29
19 to 20
Strength to Weight: Bending, points 25
19 to 20
Thermal Diffusivity, mm2/s 11
12
Thermal Shock Resistance, points 23
16 to 17

Alloy Composition

Aluminum (Al), % 0 to 0.040
0
Carbon (C), % 0.17 to 0.23
0 to 0.2
Chromium (Cr), % 3.0 to 3.3
0 to 0.3
Copper (Cu), % 0 to 0.3
0 to 0.3
Iron (Fe), % 93.8 to 95.4
96.4 to 98.7
Manganese (Mn), % 0.3 to 0.5
0.9 to 1.5
Molybdenum (Mo), % 0.5 to 0.6
0.45 to 0.6
Nickel (Ni), % 0 to 0.3
0 to 0.3
Nitrogen (N), % 0
0 to 0.012
Phosphorus (P), % 0 to 0.025
0 to 0.015
Silicon (Si), % 0.15 to 0.35
0 to 0.4
Sulfur (S), % 0 to 0.010
0 to 0.0050
Vanadium (V), % 0.45 to 0.55
0