EN 1.7779 Steel vs. Nickel 825
EN 1.7779 steel belongs to the iron alloys classification, while nickel 825 belongs to the nickel alloys. They have a modest 34% of their average alloy composition in common, which, by itself, doesn't mean much. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is EN 1.7779 steel and the bottom bar is nickel 825.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 16 | |
| 34 |
| Fatigue Strength, MPa | 430 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 78 |
| Shear Strength, MPa | 500 | |
| 430 |
| Tensile Strength: Ultimate (UTS), MPa | 810 | |
| 650 |
| Tensile Strength: Yield (Proof), MPa | 660 | |
| 260 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 300 |
| Maximum Temperature: Mechanical, °C | 470 | |
| 980 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1400 |
| Melting Onset (Solidus), °C | 1420 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 460 |
| Thermal Conductivity, W/m-K | 39 | |
| 11 |
| Thermal Expansion, µm/m-K | 13 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.7 | |
| 1.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.9 | |
| 1.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 4.0 | |
| 41 |
| Density, g/cm3 | 7.8 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 7.2 |
| Embodied Energy, MJ/kg | 41 | |
| 100 |
| Embodied Water, L/kg | 64 | |
| 230 |
Common Calculations
| PREN (Pitting Resistance) | 5.0 | |
| 31 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 120 | |
| 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1150 | |
| 170 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 29 | |
| 22 |
| Strength to Weight: Bending, points | 25 | |
| 20 |
| Thermal Diffusivity, mm2/s | 11 | |
| 2.9 |
| Thermal Shock Resistance, points | 23 | |
| 17 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.040 | |
| 0 to 0.2 |
| Carbon (C), % | 0.17 to 0.23 | |
| 0 to 0.050 |
| Chromium (Cr), % | 3.0 to 3.3 | |
| 19.5 to 23.5 |
| Copper (Cu), % | 0 to 0.3 | |
| 1.5 to 3.0 |
| Iron (Fe), % | 93.8 to 95.4 | |
| 22 to 37.9 |
| Manganese (Mn), % | 0.3 to 0.5 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0.5 to 0.6 | |
| 2.5 to 3.5 |
| Nickel (Ni), % | 0 to 0.3 | |
| 38 to 46 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0.15 to 0.35 | |
| 0 to 0.050 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.030 |
| Titanium (Ti), % | 0 | |
| 0.6 to 1.2 |
| Vanadium (V), % | 0.45 to 0.55 | |
| 0 |