EN 1.8062 Steel vs. SAE-AISI M7 Steel
Both EN 1.8062 steel and SAE-AISI M7 steel are iron alloys. They have 84% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is EN 1.8062 steel and the bottom bar is SAE-AISI M7 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 72 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 660 to 1910 | |
| 760 to 2210 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 270 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1560 |
| Melting Onset (Solidus), °C | 1400 | |
| 1510 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 450 |
| Thermal Conductivity, W/m-K | 43 | |
| 28 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.4 | |
| 18 |
| Density, g/cm3 | 7.7 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 8.9 |
| Embodied Energy, MJ/kg | 20 | |
| 130 |
| Embodied Water, L/kg | 49 | |
| 100 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 24 to 69 | |
| 26 to 76 |
| Strength to Weight: Bending, points | 22 to 44 | |
| 23 to 47 |
| Thermal Diffusivity, mm2/s | 12 | |
| 7.8 |
| Thermal Shock Resistance, points | 20 to 57 | |
| 24 to 69 |
Alloy Composition
| Carbon (C), % | 0.42 to 0.5 | |
| 1.0 to 1.1 |
| Chromium (Cr), % | 0.5 to 0.8 | |
| 3.5 to 4.0 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Iron (Fe), % | 95.9 to 97.1 | |
| 79.8 to 83.8 |
| Manganese (Mn), % | 0.5 to 0.8 | |
| 0.15 to 0.4 |
| Molybdenum (Mo), % | 0.2 to 0.3 | |
| 8.2 to 9.2 |
| Nickel (Ni), % | 0 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.030 |
| Silicon (Si), % | 1.3 to 1.7 | |
| 0.2 to 0.55 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.030 |
| Tungsten (W), % | 0 | |
| 1.4 to 2.1 |
| Vanadium (V), % | 0 | |
| 1.8 to 2.3 |