EN 1.8505 Steel vs. AWS ERNiCrMo-3
EN 1.8505 steel belongs to the iron alloys classification, while AWS ERNiCrMo-3 belongs to the nickel alloys. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is EN 1.8505 steel and the bottom bar is AWS ERNiCrMo-3.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 13 | |
| 34 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 79 |
| Tensile Strength: Ultimate (UTS), MPa | 1050 | |
| 870 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 330 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1480 |
| Melting Onset (Solidus), °C | 1410 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 440 |
| Thermal Conductivity, W/m-K | 39 | |
| 11 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.5 | |
| 1.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.7 | |
| 1.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.8 | |
| 80 |
| Density, g/cm3 | 7.8 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 1.6 | |
| 14 |
| Embodied Energy, MJ/kg | 22 | |
| 190 |
| Embodied Water, L/kg | 65 | |
| 290 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 23 |
| Strength to Weight: Axial, points | 37 | |
| 28 |
| Strength to Weight: Bending, points | 30 | |
| 24 |
| Thermal Diffusivity, mm2/s | 11 | |
| 2.8 |
| Thermal Shock Resistance, points | 31 | |
| 25 |
Alloy Composition
| Aluminum (Al), % | 0.8 to 1.2 | |
| 0 to 0.4 |
| Carbon (C), % | 0.28 to 0.35 | |
| 0 to 0.010 |
| Chromium (Cr), % | 1.5 to 1.8 | |
| 20 to 23 |
| Copper (Cu), % | 0 | |
| 0 to 0.5 |
| Iron (Fe), % | 95.4 to 97.1 | |
| 0 to 5.0 |
| Manganese (Mn), % | 0.4 to 0.7 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 0.2 to 0.4 | |
| 8.0 to 10 |
| Nickel (Ni), % | 0 | |
| 58 to 68.9 |
| Niobium (Nb), % | 0 | |
| 3.2 to 4.2 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.035 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 | |
| 0 to 0.4 |
| Residuals, % | 0 | |
| 0 to 0.5 |