EN 1.8507 Steel vs. R60804 Alloy

EN 1.8507 steel belongs to the iron alloys classification, while R60804 alloy belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is EN 1.8507 steel and the bottom bar is R60804 alloy.

EN 1.8507 (34CrAlMo5-10) Nitriding Steel UNS R60804 Zirconium-Tin Alloy

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		190
Elastic (Young's, Tensile) Modulus, GPa		98

Elongation at Break, %		16
Elongation at Break, %		22

Poisson's Ratio		0.29
Poisson's Ratio		0.34

Shear Modulus, GPa		72
Shear Modulus, GPa		36

Tensile Strength: Ultimate (UTS), MPa		900
Tensile Strength: Ultimate (UTS), MPa		430

Tensile Strength: Yield (Proof), MPa		670
Tensile Strength: Yield (Proof), MPa		270

Thermal Properties

Latent Heat of Fusion, J/g		250
Latent Heat of Fusion, J/g		250

Specific Heat Capacity, J/kg-K		480
Specific Heat Capacity, J/kg-K		270

Thermal Conductivity, W/m-K		41
Thermal Conductivity, W/m-K		22

Thermal Expansion, µm/m-K		13
Thermal Expansion, µm/m-K		6.0

Otherwise Unclassified Properties

Density, g/cm³		7.8
Density, g/cm³		6.5

Embodied Water, L/kg		63
Embodied Water, L/kg		290

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m³		130
Resilience: Ultimate (Unit Rupture Work), MJ/m³		85

Resilience: Unit (Modulus of Resilience), kJ/m³		1210
Resilience: Unit (Modulus of Resilience), kJ/m³		380

Stiffness to Weight: Axial, points		13
Stiffness to Weight: Axial, points		8.3

Stiffness to Weight: Bending, points		24
Stiffness to Weight: Bending, points		23

Strength to Weight: Axial, points		32
Strength to Weight: Axial, points		18

Strength to Weight: Bending, points		27
Strength to Weight: Bending, points		19

Thermal Diffusivity, mm²/s		11
Thermal Diffusivity, mm²/s		12

Thermal Shock Resistance, points		26
Thermal Shock Resistance, points		53

Alloy Composition

Aluminum (Al), %		0.8 to 1.2
Aluminum (Al), %		0

Carbon (C), %		0.3 to 0.37
Carbon (C), %		0

Chromium (Cr), %		1.0 to 1.3
Chromium (Cr), %		0.070 to 0.13

Iron (Fe), %		96.1 to 97.7
Iron (Fe), %		0.18 to 0.24

Manganese (Mn), %		0.4 to 0.7
Manganese (Mn), %		0

Molybdenum (Mo), %		0.15 to 0.25
Molybdenum (Mo), %		0

Phosphorus (P), %		0 to 0.025
Phosphorus (P), %		0

Silicon (Si), %		0 to 0.4
Silicon (Si), %		0

Sulfur (S), %		0 to 0.035
Sulfur (S), %		0

Tin (Sn), %		0
Tin (Sn), %		1.2 to 1.7

Zirconium (Zr), %		0
Zirconium (Zr), %		97.8 to 98.6

Residuals, %		0
Residuals, %		0 to 0.12