EN 1.8515 Steel vs. EN 1.4581 Stainless Steel

Both EN 1.8515 steel and EN 1.4581 stainless steel are iron alloys. They have 71% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.8515 steel and the bottom bar is EN 1.4581 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 340
150
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 11
28
Fatigue Strength, MPa 580
150
Impact Strength: V-Notched Charpy, J 29
45
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
78
Tensile Strength: Ultimate (UTS), MPa 1130
510
Tensile Strength: Yield (Proof), MPa 940
210

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 470
990
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 40
15
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.7
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 3.5
21
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.6
4.2
Embodied Energy, MJ/kg 22
59
Embodied Water, L/kg 60
160

Common Calculations

PREN (Pitting Resistance) 4.4
26
Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
120
Resilience: Unit (Modulus of Resilience), kJ/m3 2310
110
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 40
18
Strength to Weight: Bending, points 31
18
Thermal Diffusivity, mm2/s 11
3.9
Thermal Shock Resistance, points 33
12

Alloy Composition

Carbon (C), % 0.28 to 0.35
0 to 0.070
Chromium (Cr), % 2.8 to 3.3
18 to 20
Iron (Fe), % 94.7 to 96.5
61.4 to 71
Manganese (Mn), % 0.4 to 0.7
0 to 1.5
Molybdenum (Mo), % 0.3 to 0.5
2.0 to 2.5
Nickel (Ni), % 0 to 0.3
9.0 to 12
Niobium (Nb), % 0
0 to 1.0
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.4
0 to 1.5
Sulfur (S), % 0 to 0.035
0 to 0.030