EN 1.8515 Steel vs. C40500 Penny Bronze

EN 1.8515 steel belongs to the iron alloys classification, while C40500 penny bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.8515 steel and the bottom bar is C40500 penny bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
110
Elongation at Break, % 11
3.0 to 49
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 74
43
Shear Strength, MPa 680
210 to 310
Tensile Strength: Ultimate (UTS), MPa 1130
270 to 540
Tensile Strength: Yield (Proof), MPa 940
79 to 520

Thermal Properties

Latent Heat of Fusion, J/g 250
200
Maximum Temperature: Mechanical, °C 470
190
Melting Completion (Liquidus), °C 1460
1060
Melting Onset (Solidus), °C 1420
1020
Specific Heat Capacity, J/kg-K 470
380
Thermal Conductivity, W/m-K 40
160
Thermal Expansion, µm/m-K 13
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
41
Electrical Conductivity: Equal Weight (Specific), % IACS 8.7
42

Otherwise Unclassified Properties

Base Metal Price, % relative 3.5
30
Density, g/cm3 7.8
8.8
Embodied Carbon, kg CO2/kg material 1.6
2.7
Embodied Energy, MJ/kg 22
43
Embodied Water, L/kg 60
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
16 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 2310
28 to 1200
Stiffness to Weight: Axial, points 13
7.2
Stiffness to Weight: Bending, points 24
18
Strength to Weight: Axial, points 40
8.5 to 17
Strength to Weight: Bending, points 31
10 to 17
Thermal Diffusivity, mm2/s 11
48
Thermal Shock Resistance, points 33
9.5 to 19

Alloy Composition

Carbon (C), % 0.28 to 0.35
0
Chromium (Cr), % 2.8 to 3.3
0
Copper (Cu), % 0
94 to 96
Iron (Fe), % 94.7 to 96.5
0 to 0.050
Lead (Pb), % 0
0 to 0.050
Manganese (Mn), % 0.4 to 0.7
0
Molybdenum (Mo), % 0.3 to 0.5
0
Nickel (Ni), % 0 to 0.3
0
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.4
0
Sulfur (S), % 0 to 0.035
0
Tin (Sn), % 0
0.7 to 1.3
Zinc (Zn), % 0
2.1 to 5.3
Residuals, % 0
0 to 0.5