EN 1.8519 Steel vs. SAE-AISI 1211 Steel
Both EN 1.8519 steel and SAE-AISI 1211 steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is EN 1.8519 steel and the bottom bar is SAE-AISI 1211 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 360 | |
| 140 to 180 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 10 | |
| 11 to 29 |
| Fatigue Strength, MPa | 630 | |
| 200 to 280 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Shear Strength, MPa | 710 | |
| 280 to 350 |
| Tensile Strength: Ultimate (UTS), MPa | 1200 | |
| 430 to 580 |
| Tensile Strength: Yield (Proof), MPa | 1030 | |
| 260 to 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 450 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 40 | |
| 52 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.4 | |
| 7.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.6 | |
| 8.0 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 3.1 | |
| 1.8 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.9 | |
| 1.4 |
| Embodied Energy, MJ/kg | 26 | |
| 18 |
| Embodied Water, L/kg | 58 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 120 | |
| 61 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2790 | |
| 180 to 550 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 43 | |
| 15 to 21 |
| Strength to Weight: Bending, points | 32 | |
| 16 to 20 |
| Thermal Diffusivity, mm2/s | 11 | |
| 14 |
| Thermal Shock Resistance, points | 35 | |
| 14 to 18 |
Alloy Composition
| Carbon (C), % | 0.27 to 0.34 | |
| 0 to 0.13 |
| Chromium (Cr), % | 2.3 to 2.7 | |
| 0 |
| Iron (Fe), % | 95.7 to 97.1 | |
| 98.7 to 99.23 |
| Manganese (Mn), % | 0.4 to 0.7 | |
| 0.6 to 0.9 |
| Molybdenum (Mo), % | 0.15 to 0.25 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0.070 to 0.12 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 |
| Sulfur (S), % | 0 to 0.035 | |
| 0.1 to 0.15 |
| Vanadium (V), % | 0.1 to 0.2 | |
| 0 |