EN 1.8522 Steel vs. S38815 Stainless Steel
Both EN 1.8522 steel and S38815 stainless steel are iron alloys. They have 67% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is EN 1.8522 steel and the bottom bar is S38815 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 220 to 380 | |
| 190 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 74 | |
| 74 |
| Tensile Strength: Ultimate (UTS), MPa | 730 to 1250 | |
| 610 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 370 |
| Maximum Temperature: Mechanical, °C | 470 | |
| 860 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1360 |
| Melting Onset (Solidus), °C | 1420 | |
| 1310 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 500 |
| Thermal Expansion, µm/m-K | 13 | |
| 15 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 4.2 | |
| 19 |
| Density, g/cm3 | 7.8 | |
| 7.5 |
| Embodied Carbon, kg CO2/kg material | 2.2 | |
| 3.8 |
| Embodied Energy, MJ/kg | 31 | |
| 54 |
| Embodied Water, L/kg | 63 | |
| 140 |
Common Calculations
| PREN (Pitting Resistance) | 6.2 | |
| 18 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 26 to 44 | |
| 22 |
| Strength to Weight: Bending, points | 23 to 33 | |
| 21 |
| Thermal Shock Resistance, points | 21 to 36 | |
| 15 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.3 |
| Carbon (C), % | 0.29 to 0.36 | |
| 0 to 0.030 |
| Chromium (Cr), % | 2.8 to 3.3 | |
| 13 to 15 |
| Copper (Cu), % | 0 to 0.1 | |
| 0.75 to 1.5 |
| Iron (Fe), % | 93.7 to 96 | |
| 56.1 to 67 |
| Manganese (Mn), % | 0.4 to 0.7 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0.7 to 1.2 | |
| 0.75 to 1.5 |
| Nickel (Ni), % | 0 to 0.3 | |
| 13 to 17 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.4 | |
| 5.5 to 6.5 |
| Sulfur (S), % | 0 to 0.035 | |
| 0 to 0.020 |
| Vanadium (V), % | 0.15 to 0.25 | |
| 0 |