EN 1.8527 Steel vs. ACI-ASTM CB30 Steel

Both EN 1.8527 steel and ACI-ASTM CB30 steel are iron alloys. They have 82% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.8527 steel and the bottom bar is ACI-ASTM CB30 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 270
210
Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
77
Tensile Strength: Ultimate (UTS), MPa 900
500
Tensile Strength: Yield (Proof), MPa 800
230

Thermal Properties

Latent Heat of Fusion, J/g 260
290
Maximum Temperature: Mechanical, °C 490
940
Melting Completion (Liquidus), °C 1460
1430
Melting Onset (Solidus), °C 1420
1380
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 41
21
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.8
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 9.0
3.0

Otherwise Unclassified Properties

Base Metal Price, % relative 4.0
10
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.7
2.3
Embodied Energy, MJ/kg 23
33
Embodied Water, L/kg 66
130

Common Calculations

PREN (Pitting Resistance) 5.7
20
Resilience: Unit (Modulus of Resilience), kJ/m3 1670
140
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 32
18
Strength to Weight: Bending, points 26
18
Thermal Diffusivity, mm2/s 11
5.6
Thermal Shock Resistance, points 26
17

Alloy Composition

Carbon (C), % 0.040 to 0.12
0 to 0.3
Chromium (Cr), % 3.7 to 4.3
18 to 21
Copper (Cu), % 0 to 0.25
0 to 1.2
Iron (Fe), % 93.2 to 95.1
72.9 to 82
Manganese (Mn), % 0.85 to 1.2
0 to 1.0
Molybdenum (Mo), % 0.4 to 0.6
0
Nickel (Ni), % 0
0 to 2.0
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.4
0 to 1.5
Sulfur (S), % 0 to 0.035
0 to 0.040