EN 1.8527 Steel vs. EN 1.4419 Stainless Steel
Both EN 1.8527 steel and EN 1.4419 stainless steel are iron alloys. They have 89% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is EN 1.8527 steel and the bottom bar is EN 1.4419 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 16 | |
| 11 to 17 |
| Fatigue Strength, MPa | 520 | |
| 230 to 680 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 74 | |
| 76 |
| Shear Strength, MPa | 550 | |
| 410 to 950 |
| Tensile Strength: Ultimate (UTS), MPa | 900 | |
| 660 to 1590 |
| Tensile Strength: Yield (Proof), MPa | 800 | |
| 370 to 1240 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 490 | |
| 790 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1440 |
| Melting Onset (Solidus), °C | 1420 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 41 | |
| 30 |
| Thermal Expansion, µm/m-K | 13 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.8 | |
| 2.8 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.0 | |
| 3.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 4.0 | |
| 8.0 |
| Density, g/cm3 | 7.8 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 1.7 | |
| 2.2 |
| Embodied Energy, MJ/kg | 23 | |
| 30 |
| Embodied Water, L/kg | 66 | |
| 110 |
Common Calculations
| PREN (Pitting Resistance) | 5.7 | |
| 16 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 | |
| 95 to 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1670 | |
| 350 to 3920 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 32 | |
| 24 to 57 |
| Strength to Weight: Bending, points | 26 | |
| 22 to 39 |
| Thermal Diffusivity, mm2/s | 11 | |
| 8.1 |
| Thermal Shock Resistance, points | 26 | |
| 23 to 55 |
Alloy Composition
| Carbon (C), % | 0.040 to 0.12 | |
| 0.36 to 0.42 |
| Chromium (Cr), % | 3.7 to 4.3 | |
| 13 to 14.5 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Iron (Fe), % | 93.2 to 95.1 | |
| 82 to 86 |
| Manganese (Mn), % | 0.85 to 1.2 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0.4 to 0.6 | |
| 0.6 to 1.0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.035 | |
| 0 to 0.015 |