EN 1.8550 Steel vs. CC498K Bronze

EN 1.8550 steel belongs to the iron alloys classification, while CC498K bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.8550 steel and the bottom bar is CC498K bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 300
78
Elastic (Young's, Tensile) Modulus, GPa 190
110
Elongation at Break, % 11
14
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 73
41
Tensile Strength: Ultimate (UTS), MPa 1000
260
Tensile Strength: Yield (Proof), MPa 760
130

Thermal Properties

Latent Heat of Fusion, J/g 250
190
Maximum Temperature: Mechanical, °C 440
170
Melting Completion (Liquidus), °C 1450
1000
Melting Onset (Solidus), °C 1410
920
Specific Heat Capacity, J/kg-K 480
370
Thermal Conductivity, W/m-K 40
73
Thermal Expansion, µm/m-K 13
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
10
Electrical Conductivity: Equal Weight (Specific), % IACS 8.8
10

Otherwise Unclassified Properties

Base Metal Price, % relative 3.4
32
Density, g/cm3 7.8
8.8
Embodied Carbon, kg CO2/kg material 1.7
3.2
Embodied Energy, MJ/kg 23
52
Embodied Water, L/kg 67
360

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
30
Resilience: Unit (Modulus of Resilience), kJ/m3 1550
72
Stiffness to Weight: Axial, points 13
6.9
Stiffness to Weight: Bending, points 24
18
Strength to Weight: Axial, points 36
8.1
Strength to Weight: Bending, points 29
10
Thermal Diffusivity, mm2/s 11
22
Thermal Shock Resistance, points 29
9.3

Alloy Composition

Aluminum (Al), % 0.8 to 1.2
0 to 0.010
Antimony (Sb), % 0
0 to 0.25
Carbon (C), % 0.3 to 0.37
0
Chromium (Cr), % 1.5 to 1.8
0
Copper (Cu), % 0
85 to 90
Iron (Fe), % 94.4 to 96.3
0 to 0.25
Lead (Pb), % 0
1.0 to 2.0
Manganese (Mn), % 0.4 to 0.7
0
Molybdenum (Mo), % 0.15 to 0.25
0
Nickel (Ni), % 0.85 to 1.2
0 to 1.0
Phosphorus (P), % 0 to 0.025
0 to 0.050
Silicon (Si), % 0 to 0.4
0 to 0.010
Sulfur (S), % 0 to 0.035
0 to 0.1
Tin (Sn), % 0
5.5 to 6.5
Zinc (Zn), % 0
3.0 to 5.0