EN 1.8819 Steel vs. EN 1.0528 Steel

Both EN 1.8819 steel and EN 1.0528 steel are iron alloys. Their average alloy composition is basically identical. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.8819 steel and the bottom bar is EN 1.0528 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 130
150
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 27
20
Fatigue Strength, MPa 200
180
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 280
320
Tensile Strength: Ultimate (UTS), MPa 440
520
Tensile Strength: Yield (Proof), MPa 270
260

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 48
48
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
2.1
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.6
1.4
Embodied Energy, MJ/kg 21
19
Embodied Water, L/kg 49
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
88
Resilience: Unit (Modulus of Resilience), kJ/m3 190
180
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 16
18
Strength to Weight: Bending, points 16
18
Thermal Diffusivity, mm2/s 13
13
Thermal Shock Resistance, points 13
16

Alloy Composition

Aluminum (Al), % 0.015 to 0.034
0
Carbon (C), % 0 to 0.15
0.27 to 0.34
Chromium (Cr), % 0 to 0.35
0 to 0.4
Copper (Cu), % 0 to 0.6
0
Iron (Fe), % 95.9 to 99.985
97.5 to 99.23
Manganese (Mn), % 0 to 1.6
0.5 to 0.8
Molybdenum (Mo), % 0 to 0.13
0 to 0.1
Nickel (Ni), % 0 to 0.35
0 to 0.4
Niobium (Nb), % 0 to 0.060
0
Nitrogen (N), % 0 to 0.017
0
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0 to 0.55
0 to 0.4
Sulfur (S), % 0 to 0.025
0 to 0.045
Titanium (Ti), % 0 to 0.060
0
Vanadium (V), % 0 to 0.1
0