EN 1.8819 Steel vs. EN 1.4509 Stainless Steel

Both EN 1.8819 steel and EN 1.4509 stainless steel are iron alloys. They have 81% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.8819 steel and the bottom bar is EN 1.4509 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 130
180
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 27
21
Fatigue Strength, MPa 200
170
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Shear Strength, MPa 280
330
Tensile Strength: Ultimate (UTS), MPa 440
530
Tensile Strength: Yield (Proof), MPa 270
260

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 400
890
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 48
25
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
3.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
13
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.6
2.8
Embodied Energy, MJ/kg 21
41
Embodied Water, L/kg 49
120

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
90
Resilience: Unit (Modulus of Resilience), kJ/m3 190
180
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 16
19
Strength to Weight: Bending, points 16
19
Thermal Diffusivity, mm2/s 13
6.8
Thermal Shock Resistance, points 13
19

Alloy Composition

Aluminum (Al), % 0.015 to 0.034
0
Carbon (C), % 0 to 0.15
0 to 0.030
Chromium (Cr), % 0 to 0.35
17.5 to 18.5
Copper (Cu), % 0 to 0.6
0
Iron (Fe), % 95.9 to 99.985
77.8 to 82.1
Manganese (Mn), % 0 to 1.6
0 to 1.0
Molybdenum (Mo), % 0 to 0.13
0
Nickel (Ni), % 0 to 0.35
0
Niobium (Nb), % 0 to 0.060
0.3 to 1.0
Nitrogen (N), % 0 to 0.017
0
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.55
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.015
Titanium (Ti), % 0 to 0.060
0.1 to 0.6
Vanadium (V), % 0 to 0.1
0