EN 1.8835 Steel vs. AWS BAg-35

EN 1.8835 steel belongs to the iron alloys classification, while AWS BAg-35 belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is EN 1.8835 steel and the bottom bar is AWS BAg-35.

EN 1.8835 (P420ML1) Steel AWS BAg-35 (P07351) Filler Metal

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		190
Elastic (Young's, Tensile) Modulus, GPa		91

Poisson's Ratio		0.29
Poisson's Ratio		0.32

Shear Modulus, GPa		73
Shear Modulus, GPa		34

Tensile Strength: Ultimate (UTS), MPa		580
Tensile Strength: Ultimate (UTS), MPa		170

Thermal Properties

Latent Heat of Fusion, J/g		250
Latent Heat of Fusion, J/g		140

Melting Completion (Liquidus), °C		1460
Melting Completion (Liquidus), °C		750

Melting Onset (Solidus), °C		1420
Melting Onset (Solidus), °C		690

Specific Heat Capacity, J/kg-K		470
Specific Heat Capacity, J/kg-K		330

Thermal Expansion, µm/m-K		13
Thermal Expansion, µm/m-K		21

Otherwise Unclassified Properties

Density, g/cm³		7.8
Density, g/cm³		8.7

Embodied Carbon, kg CO₂/kg material		1.6
Embodied Carbon, kg CO₂/kg material		35

Embodied Energy, MJ/kg		21
Embodied Energy, MJ/kg		550

Common Calculations

Stiffness to Weight: Axial, points		13
Stiffness to Weight: Axial, points		5.8

Stiffness to Weight: Bending, points		24
Stiffness to Weight: Bending, points		17

Strength to Weight: Axial, points		21
Strength to Weight: Axial, points		5.4

Strength to Weight: Bending, points		20
Strength to Weight: Bending, points		7.8

Thermal Shock Resistance, points		17
Thermal Shock Resistance, points		6.4

Alloy Composition

Aluminum (Al), %		0.020 to 0.040
Aluminum (Al), %		0

Carbon (C), %		0 to 0.16
Carbon (C), %		0

Copper (Cu), %		0
Copper (Cu), %		31 to 33

Iron (Fe), %		96.7 to 99.98
Iron (Fe), %		0

Manganese (Mn), %		0 to 1.7
Manganese (Mn), %		0

Molybdenum (Mo), %		0 to 0.2
Molybdenum (Mo), %		0

Nickel (Ni), %		0 to 0.5
Nickel (Ni), %		0

Niobium (Nb), %		0 to 0.050
Niobium (Nb), %		0

Nitrogen (N), %		0 to 0.020
Nitrogen (N), %		0

Phosphorus (P), %		0 to 0.020
Phosphorus (P), %		0

Silicon (Si), %		0 to 0.5
Silicon (Si), %		0

Silver (Ag), %		0
Silver (Ag), %		34 to 36

Sulfur (S), %		0 to 0.0080
Sulfur (S), %		0

Titanium (Ti), %		0 to 0.050
Titanium (Ti), %		0

Vanadium (V), %		0 to 0.1
Vanadium (V), %		0

Zinc (Zn), %		0
Zinc (Zn), %		31 to 35

Residuals, %		0
Residuals, %		0 to 0.15